Abstract:Deformation processing is a commonly used strategy to improve the microstructure and hence mechanical properties of biodegradable Zn alloys. However, a single conventional processing method is usually limited in achieving this goal. In this work, hot extrusion combined with room-temperature equal channel angular pressing (ECAP) was used to fabricate biodegradable Zn–Cu–Li alloy. Compared to the hot-extruded alloy, the further ECAPed alloys have significantly finer Zn grains and precipitate more submicron- and nano-sized ε -CuZn 4 particles. Moreover, the 4-pass as-ECAPed alloy exhibits the best comprehensive mechanical properties with yield strength of 315 ± 3 MPa, ultimate tensile strength of 444 ± 13 MPa and elongation of 81 ± 5%, which are 13.3%, 38.8% and 72.3% higher than those of the hot-extruded alloy, respectively. In addition, in vitro and in vivo tests were performed on the 4-pass as-ECAPed alloy to evaluate its corrosion behavior, antibacterial property, cytotoxicity and biocompatibility. In vitro results showed that the 4-pass as-ECAPed alloy exhibits better corrosion resistance than the 8-pass alloy. Also, it shows good antibacterial property, hemocompatibility and cytocompatibility. In vivo results demonstrated that the 4-pass as-ECAPed alloy exhibits faster and more uniform degradation than the pure Zn (as a control group). Both the pure Zn and 4-pass as-ECAPed alloy promote formation of new bone, the mass of which increases over time. The 4-pass as-ECAPed alloy shows slightly weaker osteogenic capacity but better overall osteointegration than the pure Zn. Furthermore, both the pure Zn and 4-pass as-ECAPed alloy exhibit good in vivo biosafety.

Enhanced Mechanical Properties of a Chip-Based Al-Si-Cu-Fe Alloy with an In-Situ Emulsion Decomposition Recycled by Solid-State Processing

Comparison Between Spark Plasma Sintering and Hot Extrusion for Solid-State Recycling of Al-Si-Cu-Fe Alloy Chips

Improving Mechanical Properties of Chips-Based Aluminum Extrudates by Composite Hot Extrusion

Mechanical behavior of hot extruded aluminum 6082 chip

Effect of Extrusion Temperature on Microstructure and Mechanical Properties of Mg–Al–Zn Alloy Prepared by Solid‐State Recycling of Mixed Waste Chips

Microstructure and mechanical properties of AZ31B magnesium alloy prepared by solid-state recycling process from chips

Study on hot deformation behavior and dynamic recrystallization mechanism of recycled Al–Zn–Mg–Cu alloy

Solid-state recycling of AZ91D magnesium alloy chips

A review on solid-state recycling of aluminum machining chips and their morphology effect on recycled part quality

Enhanced comprehensive performance via alloying and rheo-diecasting in a semi-solid Al–Si–Fe–Mg–Cu–Sr alloy

Recycling of Az91 Mg Alloy Through Consolidation of Machined Chips by Extrusion and Ecap

Consolidation behavior of Mg–10Gd–2Y–0.5Zr chips during solid-state recycling

Effect of extrusion temperature on microstructure and mechanical properties of Mg-8.5Gd-2.3Y-l.8Ag- 0.4Zr alloy solid state recycled by hot extrusion

Mechanical Properties and Corrosion Resistance of Mg–10Gd–2Y–0.5Zr Alloy by Hot Extrusion Solid-State Recycling

Effect of Initial Fe Content on Microstructure and Mechanical Properties of Recycled Al-7.0Si-Fe-Mn Alloys with Constant Mn/Fe Ratio

Integrated Extrusion–Shear Forming Process of the Solid-State Recycled AZ80 Magnesium Alloy Via Hot Press Sintering

A Novel Method for Improving the Microstructure and Properties of Al-Si-Cu Alloys Based on Rapid Solidification/Powder Metallurgy

Enhanced Combination of Strength and Ductility in Ultrafine-Grained Aluminum Composites Reinforced with High Content Intragranular Nanoparticles

A novel method for improving the microstructure and the properties of Al-Si-Cu alloys prepared using rapid solidification/powder metallurgy

Effect of ultrasonic melt processing and cooling rate on microstructure evolution of Al–Cu–Mn–Mg–Fe–Si alloy

An in vitro and in vivo study of biodegradable Zn–Cu–Li alloy with high strength and ductility fabricated by hot extrusion combined with room-temperature ECAP