(Sr1-Xcax)(2)tio4 Microwave Dielectric Ceramics with R-P Structure (X=0.0.15)

Iqra Hameed,Bing Liu,Lei Li,Xiao Qiang Liu,Xiang Ming Chen

DOI: https://doi.org/10.1111/ijac.13159

2018-01-01

International Journal of Applied Ceramic Technology

Abstract:(Sr1-xCax)(2)TiO4 ceramics (0 <= x <= 0.15) were synthesized by a standard solid state reaction route. Tetragonal Ruddlesden-Popper (R-P) solid solutions (Sr1-xCax)(2)TiO4 with space group I4/mmm were obtained in the composition range of x = 00.15, while Sr3Ti2O7 has been observed as secondary phase in x <= 0.10. In the present ceramics, both the dielectric constant e(r) and temperature coefficient of resonant frequency tau(f) decreased at first and turned to increase again with increasing x, while the quality factor Qf decreased slightly at first and turned to decrease sharply after x = 0.1. The improved microwave dielectric properties with the best combination were obtained in (Sr1-xCax)(2)TiO4 ceramics at x = 0.075: e(r) = 39.3, Qf = 93 550 GHz, tau(f) = 119 ppm/degrees C The obvious improvement was achieved in temperature coefficient of resonant frequency (from 140 to 119 ppm/degrees C) with Ca2+-substitution for Sr2+ in Sr2TiO4 ceramics due to the increased B-site bond valance.