Hierarchical Formation Mechanism of Anisotropic Magnetite Microflakes and Their Superior Microwave Attenuation Properties

Zhihong Yang,Meng Li,Yu Zhang,Xujian Lyu,Dinghua Hu
DOI: https://doi.org/10.1016/j.jallcom.2018.12.139
IF: 6.2
2018-01-01
Journal of Alloys and Compounds
Abstract:In the preparation of the alpha-Fe2O3 particles, the size, thickness, morphology and size distribution were controlled by adding silicon and magnesium salts as surfactants, and finally the fine hexagonal alpha-Fe2O3 microflakes with a diameter of 1.8 mu m and a thickness of 200 nm were obtained. This synthesis method provides some ideas for the manufacture of well-defined alpha-Fe2O3 particles. In-plane aligned composites made from reduced microflakes were prepared by a vacuum infiltration method. The hysteresis loops of the composites with in-plane alignment of the microflakes were obtained by applying the external magnetic field parallel and perpendicular to the composite sample plane. It is obviously exhibited that the composites are easily magnetized along the sample plane. According to the results of magnetic and microwave measurement, aligned composites have higher permeability and magnetic loss, which lead to a better microwave absorption performance than that of random composites. Especially when the thickness is 5 mm, the minimum RL value of aligned composites (-41.67 dB) is enhanced by 258%, compared with that of random composites (-16.11 dB). This would open up the possibility of using the in-plane alignment method to improve the microwave absorbing property and expand the range of practical applications of absorbers. (C) 2018 Elsevier B.V. All rights reserved.
What problem does this paper attempt to address?