Boosting the Local Temperature of Hybrid Prussian Blue/NiO Nanotubes by Solar Light: Effect on Energy Storage
Yongxin Lu,Jingwen Xu,Chenxi Zhao,Zhida Gao,Yan-Yan Song
DOI: https://doi.org/10.1021/acssuschemeng.1c03483
2021-08-24
Abstract:Energy storage devices based on pseudocapacitive materials usually suffer from poor performance at lower temperatures. To address this challenge, in this study, we integrate a Prussian blue analog (PBA) shell on a pseudocapacitive material to achieve a remarkably improved capacitive performance by a solar light-induced heating effect. The capacitor material is prepared by growing a layer of nickel hexacyanoferrate nanocrystals on NiO nanotubes (NTs) via a simple anion-displacement reaction. The electrodes based on optimized PBA/NiO NTs not only exhibit an enhanced capacitance in a natural Li2SO4 aqueous electrolyte but also show a remarkable overall photo-to-thermal conversion efficiency. Most importantly, the local surface temperature can rapidly increase from −4.0 °C to 45.6 °C by solar-light irradiation for only 30 min. Benefitting from the highly increased local temperature, the cation storage ability is highly improved, which shows 377.8% enhancement of specific capacitance at a coulombic efficiency higher than 100%. An asymmetric supercapacitor cell assembled using PBA/NiO NTs and active carbon exhibits distinct thermally enhanced capacitance, mechanical flexibility, and outstanding cycling performance of 15,000 cycles without any capacity decay, indicating the great potential in real application for antidecay of energy storage devices in cold weather. This design paves new pathways to utilize solar light to achieve a suitable working temperature for pseudocapacitors in a low temperature environment (down to approximately −4 °C), thus possessing great application potentials in the field of advanced energy storage devices.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acssuschemeng.1c03483.SEM images and XRD analysis of Ni-Asp and NiO NT samples; SEM and EDS mapping images of a single PBA/NiO NT; SEM images of fractured NiO and PBA/NiO NT; TEM images of the double-walled structure of PBA/NiO NT; Raman spectra of NiO NTs; FT-IR spectra of Ni-Asp NTs, NiO NTs, and PBA/NiO NTs; nitrogen adsorption–desorption isotherms and pore size distribution of NiO NTs and PBA/NiO NTs; high-resolution XPS spectra of C 1s, N 1s, O 1s, and K+ of PBA/NiO NTs; EIS analysis of NiO and PBA/NiO NTs; electrochemical performance of PBA/NiO NTs in different electrolytes; CV curves of NiO NTs prepared under different temperatures; CV curves and GCD curves of NiO NTs and PBA/NiO NTs; CV curves of PBA/NiO NTs at different scan rates; GCD curves of PBA/NiO NTs at different densities; corresponding specific capacitance changes calculated from CV curves and GCD curves; coulombic efficiency calculated from the GCD curves at different current densities; capacity retention of PBA/NiO NTs; electrochemical test of samples in a 1 M KOH electrolyte; UV–vis–NIR absorbance spectra of ITO samples coated with NiO and PBA/NiO NTs; in situ absorbance curves recorded at 550 nm switched between 0.0 V and 1.0 V; temperature changes of blank ITO substrate-, NiO NT-, and PBA/NiO NT-coated ITO slides in the colored state; infrared images of PBA/NiO NTs after different NIR-laser irradiation times; GCD curves of PBA/NiO NTs under 0.5 W cm–2 NIR-laser irradiation at 5 A g–1 for 600 s; GCD curves at different irradiation times of PBA/NiO NTs under NIR-laser irradiation; capacity retention and coulombic efficiency of PBA/NiO NTs under different irradiation times; GCD curves of PBA/NiO NTs at 0.1 and 0.3 W cm–2 NIR-laser irradiation for 600 s; GCD curves after irradiation with different NIR-laser intensities for 600 s; EIS measurements under irradiation with different NIR-laser power densities and different applied electrolyte temperatures in the dark; reversibility test of PBA/NiO NT samples switching between low, high, and low temperatures; GCD curves of NiO NTs at different applied electrolyte temperatures in the dark; corresponding specific capacitance retention of NiO NTs at different applied electrolyte temperatures calculated from the GCD curves; comparison of GCD curves of NiO NTs in the dark and under 0.5 W cm–2 NIR-laser irradiation; corresponding calculated coulombic efficiency at 0, 20, and 40 °C of electrolyte solution in the dark and heated by the PBA/NiO NT electrode under solar irradiation; CV curves of the PBA/NiO NT sample under 30 min solar irradiation; CV curves under different solar irradiation times and at different electrolyte temperatures; specific capacitance percentage after different solar irradiation times; photocatalytic degradation of PBA/NiO NTs under 808 nm laser-light irradiation; ion diffusion coefficient experiment of PBA/NiO NTs during charging and discharging; GCD curves at different current densities of the ASC; GCD curves of the ASC at different bending angles; and cycling stability test of the as-prepared ASC (PDF)This article has not yet bee -Abstract Truncated-
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology