Mechanical Activation Enhanced Solid-State Synthesis of NaCrO2 Cathode Material

Mei Luo,Angel L. Ortiz,Fangmin Guo,Zhepu Shi,Ling Li,Yang Ren,Xiaoyi Zhang,Zonghai Chen,Leon L. Shaw,Wei Chen

DOI: https://doi.org/10.1016/j.mtla.2018.11.021

2018-01-01

Materialia

Abstract:NaCrO2 has been studied lately as a promising cathode material for Na-ion batteries. Consequently, we have conducted the first investigation on how high-energy ball milling before the high temperature reaction influences the synthesis reaction of NaCrO2 derived from the typical Na2CO3 and Cr2O3 reactants. In-situ synchrotron X-ray diffractometry is employed for the first time to provide a comprehensive understanding of the critical reaction temperatures and reaction pathway. It is found that high-energy ball milling at room temperature can result in significant changes in the synthesis reaction of NaCrO2 when compared to reactants without high-energy ball milling. These changes include a decreased onset temperature for the formation of O-3-NaCrO2, an increased reaction kinetics, an alternation of the reaction pathway, and a complete reaction at 900 degrees C to form thermally-stable O-3-NaCrO2 phase. These phenomena have been ascribed to the mechanical activation induced by high-energy ball milling before high temperature reaction. In contrast, without high-energy ball milling the reaction product at 900 degrees C is a highly impure NaCrO2 with a poor thermal stability. The thermally-stable O-3-NaCrO2 powder produced with mechanical activation of the reactants at RT has much higher specific capacity (similar to 115 mAh/g) than the Na-deficient NaCrO2 powder with unreacted Cr2O3 generated without mechanical activation of the reactants at RT. Furthermore, the thermally-stable O-3-NaCrO2 powder exhibits the best capacity retention among all the NaCrO2 without coatings reported so far in the literature.