Optimizing Mechanical Properties of Gradient-Structured Low-Carbon Steel by Manipulating Grain Size Distribution

Lina Wang,Bin Li,Yindong Shi,Guangwei Huang,Wenpeng Song,Shaoyuan Li

DOI: https://doi.org/10.1016/j.msea.2018.11.042

2019-01-01

Abstract:In this paper, various gradient structures (i.e., the ferrite grain size increases continuously with the depth) with different grain size distributions are produced in low-carbon steel by using pre-torsion deformation and thermal annealing at similar to 550 degrees C to 700 degrees C for 0.5 h. Results indicate that the grain size distribution possesses a crucial influence on mechanical properties of gradient-structured samples. The yield strength decreases steady accompanied by a gradual increase in uniform ductility and static toughness with increasing the ferrite grain size. The optimal synergy of high yield strength (sigma(y)similar to 506.0 +/- 3.9 MPa), promising uniform ductility (epsilon(u)similar to 9.6 +/- 0.5%) and static toughness (U-r similar to 108.8 +/- 4.1 MJ/m(3)) is achieved by a specific gradient structure with the grain size distribution from similar to 7.2 mu m at the surface to similar to 16.5 mu m at the core, which is much better than that (sigma(y)similar to 318.2 +/- 1.6 MPa, epsilon(u)similar to 13.4 +/- 0.4% and U-r similar to 102.5 +/- 4.8 MJ/m(3)) of its coarse-grained (CG) counterpart. Related strengthening and toughening mechanisms are also discussed.