Abstract:The NiCoCrAlYHf coating has been widely used as a bond layer in thermal barrier coating system, of which the oxidation behaviors and surface roughening mechanisms in service are greatly influenced by pre-treatment temperature. To clarify the effects of pre-treatment temperatures, the characteristics of the pre-treated coatings and isothermally exposed coatings were characterized and analyzed, including microstructure, weight change, TGO thickness and surface roughness . When the pre-treatment temperature was relatively low, the coating surface did not form a TGO with integrity. When the pre-treatment temperature was relatively high, mixed oxides were generated on the coating surface during the pre-treatment process, which damaged the integrity of TGO. The overall performance of the coatings pretreated at too high or low temperatures was insufficient. Moreover, the phase transformation of coating is strongly correlated with diffusion of Al element. The pre-treatment process could change the as-deposited coating from a single-phase to a duplex-phase structure due to the diffusion of Al element. In the oxidation process, the duplex-phase structure changed to a single-phase structure due to the consumption of Al element. In addition, it was found that there was a competitive relationship between grain sliding caused by high-temperature stress and Al 2 O 3 growth in the coating depression, which was one of the main surface roughening mechanisms of NiCoCrAlYHf coating.

Effects of the Β Phase Size and Shape on the Oxidation Behavior of NiCoCrAlY Coating

Different Growth Mechanisms of Alumina on the Surface of NiPtAl and MCrAlY Bondcoatings in EB-PVD TBC System

A High Performance NiCoCrAlY Bond Coat Manufactured Using Laser Powder Deposition

Study of the Effect of Laser Treatment on the Initial Oxidation Behaviour of Al‐coated NiCrAlY Bond‐coat

Temperature Effect on Early Oxidation Behavior of NiCoCrAlY Coatings: Microstructure and Phase Transformation

Effect of microstructure of a NiCoCrAlY coating fabricated by high-velocity air fuel on the isothermal oxidation

High-temperature performance of Pt-modified Ni-20Co-28Cr-10Al-0.5Y coating: Formation mechanism of Pt-rich overlayer and its effect on thermally grown oxide failure

Pt-modification on the thermal cycling behavior of NiCoCrAlYTa coating: a case study

Investigation on the Oxidation Behavior of the NiCrAlY Bond-Coat with Low Al Content Sprayed by High Velocity Oxygen Fuel Method

Effect of aluminisation characteristics on the microstructure of single phase β-(Ni,Pt)Al coating and the isothermal oxidation behaviour

Effect of pre-treatment temperatures on the oxidation behaviors and surface roughening mechanisms of NiCoCrAlYHf coating

Co-doping Effect of Hf and Y on Improving Cyclic Oxidation Behavior of (ni,pt)al Coating at 1150 °C

A study on the thermal cyclic behavior of NiCrAlY coatings via femtosecond laser remelting with high repetition rate

High Temperature Oxidation Behavior of NiCoCrAlFeY High Entropy Bond Coating Fabricated by High-Speed Laser Cladding

Effect of Powder Structure on Microstructure of the Oxide Scales Formed on Cold-Sprayed Nicraly Coatings

Microstructure features of cold-sprayed NiCoCrAlTaY coating and its high temperature oxidation behavior

Oxidation Behavior of Nanostructured NiCrAlY Coating Deposited by Cold Spray

Improving the oxidation behavior of low expansion Ni + CrAlYNO coating systems by regulating the oxygen content

Effect of Depositing Al on High-Temperature Oxidation Behavior of NiCrAlY Bond

Effect of Al Plating on Growth Behavior of TGO Layer in CoCrNiAlY–YSZ–RSZ Dual-Ceramic Coating

Cyclic oxidation and rumpling behaviour of single phase β-(Ni,Pt)Al coatings with different thickness of initial Pt plating