Optical thermometry based on the stark sub-levels of Er3+ in Y2Mo3O12: Yb3+, Er3+ particles synthesized by sol–gel method
Yubin Wang,Zhanhui Liu,Haiqing Liu,Siyu Chen,Juhong Miao,Wei-feng Rao
DOI: https://doi.org/10.1007/s10854-024-12804-0
2024-05-30
Journal of Materials Science Materials in Electronics
Abstract:To settle the challenges of both excellent luminescent property and high sensitivity for optical thermometry, a series of Y 2 Mo 3 O 12 : Yb 3+ , Er 3+ submicron particles with different Yb 3+ contents were prepared via a citric-assisted sol–gel technique. Under 980 nm excitation, the samples exhibit characteristic emissions ascribed to the transitions of 2 H 11/2 and 4 S 3/2 levels to the ground state of Er 3+ ion. The Stark splitting of 4 S 3/2 and 2 H 11/2 is observed. According to the emission spectra, the optimal doping concentration of Yb 3+ and Er 3+ is concluded to be 15 mol% and 1 mol%, respectively. Then, the temperature-dependent luminescent behavior of Y 2 Mo 3 O 12 : 15%Yb 3+ , 1%Er 3+ sample was further investigated, which exhibits good temperature stability with a slight decrease as temperature rises. Based on the fluorescence intensity ratio technique, the maximal absolute sensitivity S A of 0.0243 K −1 and relative sensitivity S R of 1.161%K −1 were achieved using the Stark sub-levels ( I H / I S2 ), which are 1.75 and 1.07 folds than that of the traditional thermal-coupled levels ( I H / I S1+S2 ) of Er 3+ ion. The results show that the Stark sub-levels can be utilized as an effect strategy to improve thermometry sensitivity and Y 2 Mo 3 O 12 : Yb 3+ , Er 3+ phosphor could be considered as a promising temperature sensing material.
engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied