Abstract:Bulk spinel Co3O4 oxide and supported Co3O4 catalysts (Co3O4/YSZ and Co3O4/TiO2) were synthesized by one-step hydrothermal method. Their physicochemical properties were characterized by inductively coupled plasma optical emission spectroscopy, N2-sorption, powder X-ray diffraction, scanning electron microscopy, transmission electron microscopy, hydrogen-temperature programmed reduction and X-ray photoelectron spectroscopy.These characterization strategies were applied to corroborate and better understand the interaction between Co3O4 and the supports induced by the synergistic effect of support and the subsequent catalytic performance in toluene oxidation. The catalytic stability was evaluated by three consecutive runs and a long-term test. A highest toluene catalytic activity was achieved over Co3O4/YSZ supported catalyst comparing to that of the bulk Co3O4 and Co3O4/TiO2 catalysts, which could be attributed to its better low-temperature reducibility, oxygen activation and mobility induced by the intrinsic support properties. Thus, the positive interaction between spinel Co3O4 phase and YSZ support promoted the intrinsic catalytic properties for toluene oxidation, which was verify by testing a dual catalyst bed system consisting of bulk Co3O4 catalyst and YSZ support beds. These results were further confirmed by temperature-programmed oxygen isotopic exchange experiments, which indicated that the activation and diffusion of oxygen species on the YSZ oxygen vacancy sites were promoted by Co3O4, resulting in a significant increase of the reaction rate for toluene oxidation.

Promotion Effect of Ga−Co Spinel Derived from Layered Double Hydroxides for Toluene Oxidation

Rational Tuning Towards A/B-sites Double-Occupying Cobalt on Tri-Metallic Spinel: Insights into Its Catalytic Activity on Toluene Catalytic Oxidation

Ga-Doped Spinel-Typed Co-Al Catalysts for Co2-Assisted Ethane Dehydrogenation

Ga-Doped MgAl2O4 Spinel As an Efficient Catalyst for Ethane Dehydrogenation to Ethylene Assisted by CO2

Pd-Co Based Spinel Oxides Derived from Pd Nanoparticles Immobilized on Layered Double Hydroxides for Toluene Combustion

Spinel Co3O4 oxides-support synergistic effect on catalytic oxidation of toluene

Enhanced ability of toluene oxidation by controlling inversion degree of spinel composed of only Co, Mn

Octahedral Co2+‐O‐Co3+ in Mixed Cobalt Spinel Promotes Active and Stable Acidic Oxygen Evolution

Enhanced Activity of Spinel-type Ga2O3–Al2O3 Mixed Oxide for the Dehydrogenation of Propane in the Presence of CO2

Promotional Effects of Sm/Ce/La Doping on Soot Oxidation over MnCo2O4 Spinel Catalysts

Effect of copper source on the structure–activity of CuAl2O4 spinel catalysts for CO hydrogenation

Dehydrogenation of propane over spinel-type gallia–alumina solid solution catalysts

Enhanced Activity of Spinel-type Ga<sub>2</sub>O<sub>3</sub>–Al<sub>2</sub>O<sub>3</sub> Mixed Oxide for the Dehydrogenation of Propane in the Presence of CO<sub>2</sub>

A bimetallic MOF-derived MnCo spinel oxide catalyst to enhance toluene catalytic degradation

The Influence of the Hydrogen Reduction on the Structure and Catalytic Activity of CoAl_2O_4 Spinel Catalysts

Low-temperature Gas-Phase Toluene Catalytic Combustion over Modified CoCr2O4 Spinel Catalysts: Effect of Co/Cr Content and Calcination Temperature

Template-free Scalable Synthesis of Flower-like Co3-x Mn x O4 Spinel Catalysts for Toluene Oxidation

Highly active urchin-like MCo2O4 (M = Co, Cu, Ni or Zn) spinel for toluene catalytic combustion

Manipulating the Spin State of Spinel Octahedral Sites via a π‐π Type Orbital Coupling to Boost Water Oxidation

Engineering High‐Spin State Cobalt Cations in Sulfide Spinel for Enhancing Water Oxidation

Effect of a Carbon Promoter on the Properties of a Co/MgAlO4 Catalyst for Fischer–Tropsch Synthesis