Abstract:Using Atomsk and LAMMPS to construct nine bicrystal Mg models with preset voids and symmetric tilt grain boundaries, tensile simulations were performed at the same rate. The results showed that as the symmetric tilt grain boundary angle increased from 20° to 30°, the yield stress decreased from 2.28 to 1.42 GPa. Based on the plastic deformation and stress–strain curves, the nine bicrystal magnesium models with different symmetric tilt grain boundaries can be divided into two groups: the first group ranges from 20° to 40°, and the second group from 45° to 80°. A representative case is selected from each group. In the first group of models, the main modes of plastic deformation are grain boundary migration, basal dislocation slip, and stacking faults; whereas in the second group, there is a higher number of basal dislocation slips, leading to a greater quantity of stacking faults, and thus a stronger capacity for plastic deformation.2 A twin‐crystal magnesium (Mg) model with 9 different symmetric tilt grain boundary (STGB) angles (20°–80°) with preset nanohole defects is established by atomsk and lammps software. The mechanical behavior of grain boundary (GB) angles on twin‐crystal Mg with cavity defects and its cavity evolution are simulated by the molecular dynamics method with embedded atomic potential, and the plastic deformation mechanism is revealed. The results show that the yield stress decreases with the increase of the STGB Angle during the stretching process. When the GB Angle increases from 20° to 80°, the yield stress decreases from 2.28 to 1.42 Gpa. This is because the larger the STGB Angle is, the larger the Schmidt factor is, and the easier it is to start dislocation slip during the stretching process. On the other hand, the larger the Angle of STGB, the more the number of atomic voids at the interface, and the more the number of dislocation nucleation points. The larger the Angle of STGB, the lower the strength of twinning Mg but the better the plasticity to avoid fracture. The plastic deformation mechanism mainly includes the nucleation of Shockley incomplete dislocation at STGBs, dislocation slip generates stacking faults (SFs), GB migration, and base plane dislocations.

Basal 〈a〉 Dislocation-{1¯011} Contraction Twin Interactions in Magnesium

The Dislocation-Twin Interaction and Evolution of Twin Boundary in AZ31 Mg Alloy

Size-Dependent Dislocation-Twin Interactions

Local Lattice Distortion Mediated Formation of Stacking Faults in Mg Alloys

Interactions Between Dislocations and Penta-Twins in Metallic Nanocrystals

Misfit strain induced phase transformation at a basal/prismatic twin boundary in deformation of magnesium

{10 1 ̄ 2 } twinning nucleation in magnesium assisted by alternative sweeping of partial dislocations via an intermediate precursor

Unconventional [math] twinning assisted by pyramidal II stacking faults

Twin-solute, twin-dislocation and twin-twin interactions in magnesium

Atomistic simulations of the interaction of basal dislocations with MgZn$_2$ precipitates in Mg alloys

Interaction between 10 1 ̄ 2 and 30 3 ̄ 4 twin in magnesium alloy

Slip transmutation between basal 〈a〉 dislocation and {112 ̄1} twinning across {112 ̄4} twin boundary in titanium

On the importance of prismatic/basal interfaces in the growth of (-1012) twins in hexagonal close-packed crystals

On the migration of {10 1 ̄ 1} and {10 1 ̄ 3} coherent twin boundaries in magnesium

Atomistic Simulations of Basal Dislocations Interacting with Mg$_{17}$Al$_{12}$ Precipitates in Mg

Disconnection-mediated twin embryo growth in Mg

Atomistic simulations of twin facets associated with three-dimensional { 1 ̄ 011 } twins in magnesium

Study on the Plastic Deformation Mechanism of Void‐Containing Twin‐Crystal Magnesium with Symmetric Tilt Grain Boundary Angles

Atomistic-informed phase field modeling of magnesium twin growth by disconnections

Dissociation of edge and screw pyramidal I and II dislocations in magnesium

Atomistic Investigation of the Effect of Non-Glide Stress on the Deformation and Dislocation Transfer at Hexagonal Close-Packed Metal Grain Boundary