Abstract:Phenolic foam (PF) displays excellent flame, smoke, and toxicity (FST) properties and good insulation properties. Nevertheless, the friability and inferior mechanical properties of PF have critically restricted its application in many fields. A series of phenolic foam/silica nanocomposites (MPF) with different silica contents were synthesized by in situ polymerization in this study. During the in situ polymerization process, the synthesis of phenolic resin/silica nanocomposites and formation of chemical bonding between the components were generated simultaneously. The reactive principle between silica nanoparticles and prepolymer was investigated using Fourier transform infrared spectroscopy (FTIR), and the results of FTIR indicated existence of the chemical reaction between them. Meanwhile, silica can act as "bridge" to form crosslinked network structure. The mechanical, thermal, and friability properties of MPF nanocomposites were characterized. Moreover, the results of microstructure of pure PF and MPFs indicated that the cell size distributions of MPFs are narrower, the cell distributions of MPFs are more uniform, and the cell wall thickness of MPFs is thicker, compared with pure PF. When the content of silica sol was 2 wt%, the compressive strength, compressive modulus, and tensile strength were increased by a factor of 47.37%, 38.55%, and 57.14% compared with that of pure PF, respectively. Furthermore, all MPF nanocomposites exhibited better thermal stability and lower pulverization ratio than that of pure PF. (C) 2015 Society of Plastics Engineers

Surface Sedimentation and Adherence of Nano‐SiO2 to Improve Thermal Stability and Flame Resistance of Melamine‐formaldehyde Foam Via Sol‐gel Method

Effortless Impregnation Method for Melamine Formaldehyde Foams Exhibiting Elevated Thermal Stability and Exceptional Flame Retardant Characteristics

Tuning thermal stability of fluorine-free foam by nano-MDH inorganic flame retardant

Thermal Stability of Gel Foams Stabilized by Xanthan Gum, Silica Nanoparticles and Surfactants

Flame retardancy and smoke suppression of silicone foams with modified microencapsulated Mg/Zn/Al-layered double hydroxide

Preparation of a nano-silica modified melamine formaldehyde resin

Thermal Stability of Gel Foams Co-Stabilized by Nano-Aluminum Hydroxide and Surfactants

Bio-based melamine formaldehyde resins for flame-retardant polyurethane foams

Ammonium polyphosphate-based nanocoating for melamine foam towards high flame retardancy and anti-shrinkage in fire

Study on Thermal Stability of Gel Foam Co-Stabilized by Hydrophilic Silica Nanoparticles and Surfactants

Preparation of a Silica Nanospheres/graphene Oxide Hybrid and Its Application in Phenolic Foams with Improved Mechanical Strengths, Friability and Flame Retardancy

Preparation and Properties of Melamine Formaldehyde Resin Modified by Functionalized Nano-Sio2 and Polyvinyl Alcohol

A Novel Elastic Urea–Melamine–Formaldehyde Foam: Structure and Properties

Fabrication of dimethyl methylphosphonate-loaded mesoporous silica nano fire extinguisher and flame retarding unsaturated polyester

Flame-Retardant and Smoke-Suppressed Silicone Foams with Chitosan-Based Nanocoatings

Preparation and Properties of Silica Gel Foam As Fire-Retardant with High Water Retention for Wood

Synthesis of Core-Shell Expandable Graphite/Melamine-Formaldehyde Particles and Their Flame Retardant Applications

Micro-nano Surface Structure Construction and Hydrophobic Modification to Prepare Efficient Oil-Water Separation Melamine Formaldehyde Foam

Preparation and Properties of Melamine-Formaldehyde Foam by Microwave Foaming

Facile fabrication of low-content surface-assembled MXene in silicone rubber foam materials with lightweight, wide-temperature mechanical flexibility, improved flame resistance and exceptional smoke suppression

Enhanced mechanical properties, thermal stability of phenolic‐formaldehyde foam/silica nanocomposites via in situ polymerization