Abstract:New lead‐free perovskite solid solution ceramics of (1 − x)(Bi1/2Na1/2)TiO3–xBa(Ni1/2Nb1/2)O3[(1−x)BNT–xBNN,x = 0.02–0.06) were prepared and their dielectric, ferroelectric, piezoelectric, and electromechanical properties were investigated as a function of the BNN content. The X‐ray diffraction results indicated that the addition of BNN has induced a morphotropic phase transformation from rhombohedral to pseudocubic symmetry approximately at x = 0.045, accompanying an evolution of dielectric relaxor behavior as characterized by enhanced dielectric diffuseness and frequency dispersion. In the proximity of the ferroelectric rhombohedral and pseudocubic phase coexistence zone, the x = 0.045 ceramics exhibited optimal piezoelectric and electromechanical coupling properties of d33~121 pC/N and kp~0.27 owing to decreased energy barriers for polarization switching. However, further addition of BNN could cause a decrease in freezing temperatures of polar nanoregions till the coexistence of nonergodic and ergodic relaxor phases occurred near room temperature, especially for the x = 0.05 sample which has negligible negative strains and thus show the maximum electrostrain of 0.3% under an external electric field of 7 kV/mm, but almost vanished piezoelectric properties. This was attributed to the fact that the induced long‐range ferroelectric order could reversibly switch back to its original ergodic state upon removal of external electric fields.

Electric Field–induced Large Strain of (bi1/2na1/2)0.935ba0.065tio3–cayalo4 Lead–free Ceramics

Enhanced Electric-Field-induced Strain in 0.7bi(1−x)smxfeo3–0.3batio3 Lead-Free Ceramics

Large electric‐field‐induced strain and enhanced piezoelectric constant in CuO‐modified BiFeO3‐BaTiO3 ceramics

Piezoelectric And Strain Properties Of Ba(Ti1-Xzrx)O-3 Ceramics

Field-induced large strain in lead-free (Bi0.5Na0.5)1−xBaxTi0.98 (Fe0.5Ta0.5)0.02O3 piezoelectric ceramics

Electric Field-Induced Large Strain in Ni/Sb-co Doped (Bi 0.5 Na 0.5 ) TiO 3 -Based Lead-Free Ceramics

Electric Field-Induced Large Strain in Ni/Sb-co Doped (bi0.5na0.5) TiO3-Based Lead-Free Ceramics

Large Strain Response in (mn,sb)–modified (bi 0.5 Na 0.5 ) 0.935 Ba 0.065 TiO 3 Lead–free Piezoelectric Ceramics

Field-induced Large Strain in Lead-Free 0.99[(1−x) Bi0.5(Na0.80K0.20)0.5TiO3–xBiFeO3]–0.01(K0.5Na0.5)NbO3 Piezoelectric Ceramics

Electric Field-Induced Giant Strain and Piezoelectricity Enhancement Effect in (bi1/2na1/2)0.935+xba0.065ti1−x(pr1/2nb1/2)xo3 Lead-Free Ceramics

High strain in (Bi1/2Na1/2)0.935Ba0.065TiO3–Sr3FeNb2O9 lead-free ceramics with giant piezoresponse

Dielectric, Ferroelectric and Field-Induced Strain Response of Lead-Free (fe, Sb)-modified (bi0.5na0.5)0.935ba0.065tio3 Ceramics

Large strain improvement of lead-free (1−x) Bi0.5Na0.42K0.08Zr0.02Ti0.98O3–xBa(Nb0.5Fe0.5)O3 piezoelectric ceramics

Large Electric-Field-induced Strain in B-site Complex-Ion (Fe0.5nb0.5)4+-Doped Bi1/2 (na0.82k0.12)1/2tio3 Lead-Free Piezoceramics

Giant electromechanical strain response in lead‐free SrTiO3‐doped (Bi0.5Na0.5TiO3–BaTiO3)–LiNbO3 piezoelectric ceramics

Large electric-field-induced strain and energy storage properties in Bi0.5Na0.5TiO3-(0.5Ba0.7Ca0.3TiO3-0.5BaTi0.8Zr0.2O3) lead-free relaxor ferroelectric ceramics

Phase‐Composition‐Dependent Piezoelectric and Electromechanical Strain Properties in (bi1/2na1/2)tio3–ba(ni1/2nb1/2)o3 Lead‐Free Ceramics

Nanoscale Ferroelectric/relaxor Composites: Origin of Large Strain in Lead–free Bi–based Incipient Piezoelectric Ceramics

Ferroelectric and Piezoelectric Properties of 0.82(bi0.5na0.5) TiO3-(0.18-x)BaTiO3-x(Bi0.5Na0.5)(Mn1/3Nb2/3)O3 Lead-Free Ceramics

Enhancement of Strain by Electrically-Induced Phase Transitions in BNKT-based Ceramics

Strain evolution from the ferroelectric to the relaxor state in (0.67 - x)BiFeO3-0.33BaTiO3- x Bi(Mg0.5Zr0.5)O3 lead-free ceramics