Insights on the Activation and Stabilization of NCA Cathode Interface: Surface Chemical State Modulations of Aluminum-Mediated Li 0.73 CoO 2 Coatings
Yao Lu,Shuai Hu,Lijun Xiong,Lishan Yang,Jun Wang,Yuanhui Pan,Shuangshuang Zhao,Yahui Yang,Chenghuan Huang,Jian Zhu,Wen-Yi Zhou,Youyuan Zhou
DOI: https://doi.org/10.1021/acssuschemeng.0c05229
2020-09-07
Abstract:Layered nickel-rich cathodes generally suffer from their unstable surface because of lithium impurities. Thus, building an interface with both high electrochemical stability and electroactivity is essential for the development of cathodes. In this work, a Li<sub>0.73</sub>Co<sub>1–<i>x</i></sub>Al<sub><i>x</i></sub>O<sub>2</sub> thin layer was successfully coated on pristine LiNi<sub>0.8</sub>Co<sub>0.15</sub>Al<sub>0.05</sub>O<sub>2</sub> (NCA) spheres by the reaction of the surface residual lithium with cobalt oxalate nanomaterials. Then, the surface chemical states of NCA were effectively modulated by Li<sub>0.73</sub>Co<sub>1–<i>x</i></sub>Al<sub><i>x</i></sub>O<sub>2</sub> coating, including less surface lithium impurities, lower resistance, enhanced ion conductivity, and cycling stability. As a potential cathode material with a higher oxidation potential than that of NCA, Li<sub>0.73</sub>Co<sub>1–<i>x</i></sub>Al<sub><i>x</i></sub>O<sub>2</sub> coating plays both roles of an isolation layer and active layer. The advances of Li<sub>0.73</sub>Co<sub>1–<i>x</i></sub>Al<sub><i>x</i></sub>O<sub>2</sub> coating may be related to the enhanced covalence property of the Co–O bond and the coexistence of Co<sup>4+</sup> and Al<sup>3+</sup>, which can help to form a stable cathode–electrolyte interface and boost the ion diffusion of the coated NCA cathode. This Li<sub>0.73</sub>Co<sub>1–<i>x</i></sub>Al<sub><i>x</i></sub>O<sub>2</sub>-modified NCA cathode exhibits a highly competitive performance, such as a capacity of 215.2 mA h g<sup>–1</sup> at the initial cycle (0.1 C) and a retention rate of 62.7% after 200 cycles at 5 C. This surface chemical state modulation strategy provides a new possibility of surface engineering with nickel-rich cathodes for high-energy Li-ion batteries.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acssuschemeng.0c05229?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acssuschemeng.0c05229</a>.XRD pattern and SEM image of the precursor; Raman spectra of NCA, , and ; HRTEM of pristine NCA; XRD patterns and structure parameters of 1.0 wt % Li<sub>0.73</sub>Co<sub>1–<i>x</i></sub>Al<sub><i>x</i></sub>O<sub>2</sub>-coated NCA (annealing temperature at 500, 600, and 700 °C); cycling performances of pristine and all experimental samples; full battery cycling test of NCA, , and ; discharge curves of NCA, , and ; XRD patterns of NCA, , and after 200 cycles; experimental design of this work; and calculated relative area of the XPS peaks of NCA, , and (<a class="ext-link" href="/doi/suppl/10.1021/acssuschemeng.0c05229/suppl_file/sc0c05229_si_001.pdf">PDF</a>).This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology