Remarkable catalysis of spinel ferrite XFe<sub>2</sub> O<sub>4</sub> ( X = Ni, Co, Mn, Cu, Zn) nanoparticles on the dehydrogenation properties of LiAlH<sub>4</sub> : An experimental and theoretical study
Sheng Wei,Jiaxi Liu,Yongpeng Xia,Huanzhi Zhang,Riguang Cheng,Lixian Sun,Fen Xu,Pengru Huang,Federico Rosei,Aleskey A. Pimerzin,Hans Juergen Seifert,Hongge Pan
DOI: https://doi.org/10.1016/j.jmst.2021.08.088
2022-01-01
Abstract:Safe, compact, lightweight and cost-effective hydrogen storage is one of the main challenges that need to be addressed to effectively deploy the hydrogen economy. LiAlH 4 , as a solid-state hydrogen storage material, presents several advantages such as high hydrogen storage capacity, low price and abundant sources. Unfortunately, neither thermodynamic nor kinetic properties of dehydrogenation for LiAlH 4 can fulfill the requirements of practical application. Thus, a series of spinel ferrite nanoparticles such as X Fe 2 O 4 ( X = Ni, Co, Mn, Cu, Zn, Fe) were prepared by using the modified thermal decomposition method, and then doped into LiAlH 4 by using ball milling. Our results show that LiAlH 4 doped with 7 wt% NiFe 2 O 4 starts to release hydrogen at 69.1 degrees C, and the total amount of hydrogen released is 7.29 wt% before 300 degrees C. The activation energies of the two-step hydrogen release reactions of LiAlH 4 doped with 7 wt% NiFe 2 O 4 are 42.32 kJ mol -1 and 71.42 kJ mol -1 , which are 59.0% and 63.6% lower than those of as-received LiAlH 4 , respectively. Combining the density functional theory (DFT) calculations, we reveal that both the presence of NiFe 2 O 4 and in-situ formed Al 4 Ni 3 in ball-milling decrease the desorption energy barrier of Al-H bonding in LiAlH 4 and accelerate the breakdown of Al-H bonding through the interfacial charge transfer and the dehybridization of the Al-H cluster. Thus, the experimental and theoretical results open a new avenue toward designing high effective catalysts applied to LiAlH 4 as a candidate for hydrogen storage.