Abstract:In this study, dense anticorrosion magnesium-aluminum layered double hydroxide (MgAl-LDH) films were prepared for the first time by introducing a cationic surfactant tetradecyltrimethyl ammonium bromide (TTAB) in the process of in situ hydrothermal synthesis of Mg-Al LDH films on an AZ31 magnesium alloy. Results of XRD, FTIR, and SEM confirmed that TTAB forms the MgAl-LDH-TTAB, although TTAB cannot enter into LDH layers, and MgAl-LDH-TTAB powders are much smaller and more homogenous than MgAl-CO32--LDH powders. Results of SEM, EDS, mapping, and XPS confirmed that TTAB forms the MgAl-LDH-TTAB films and endows LDH films with denser structure, which provides films with better shielding efficiency. Results of potentiodynamic polarization curves (PDP) and electrochemical impedance spectroscopy (EIS) confirmed that MgAl-LDH-TTABx g films have better corrosion resistance than an MgAl-CO32--LDH film. The corrosion current density (icorr) of the MgAl-LDH-TTAB0.35 g film in 3.5 wt.% NaCl solution was reduced to 1.09 × 10-8 A.cm-2 and the |Z|f = 0.05 Hz value was increased to 4.48 × 105 Ω·cm2. Moreover, the increasing concentration of TTAB in MgAl-LDH-TTABx g (x = 0.025, 0.05, 0.1, 0.2 and 0.35) provided denser outer layer LDH films and thereby increased the corrosion resistance of the AZ31 Mg alloy. Additionally, the |Z|f = 0.05 Hz values of the MgAl-LDH-TTAB0.35 g film still remained at 105 Ω·cm2 after being immersed in 3.5 wt.% NaCl solution for 168 h, implying the good long-term corrosion resistance of MgAl-LDH-TTABx g films. Therefore, introducing cationic surfactant in the process of in situ hydrothermal synthesis can be seen as a novel approach to creating efficient anticorrosion LDH films for Mg alloys.

Communication-Fabrication of Protective Layered Double Hydroxide Films by Conversion of Anodic Films on Magnesium Alloy

A Novel Approach to Fabricate Protective Layered Double Hydroxide Films on the Surface of Anodized Mg‐Al Alloy

Fabrication and Characterization of Mg-M Layered Double Hydroxide Films on Anodized Magnesium Alloy AZ31

Fabrication of oriented layered double hydroxide films by spin coating and their use in corrosion protection

Growth Behavior of MgAl-layered Double Hydroxide Films by Conversion of Anodic Films on Magnesium Alloy AZ31 and Their Corrosion Protection

Enhanced Protective Zn–Al Layered Double Hydroxide Film Fabricated on Anodized 2198 Aluminum Alloy

Preparation of one-step organic anion-modified MgAl-LDH films under mild conditions for Mg alloy corrosion protection

Growth Mechanism and Corrosion Resistance of Layered Double Hydroxide Film on Magnesium Alloy Without External Addition of Magnesium and Aluminum Salts

Influence of Mg substrate on the formation mechanism and corrosion resistance of LDH films

Doublely-doped Mg-Al-Ce-V2O74- LDH Composite Film on Magnesium Alloy AZ31 for Anticorrosion

Active Corrosion Protection of Mg–Al Layered Double Hydroxide for Magnesium Alloys: A Short Review

In-situ Grown Super- or Hydrophobic Mg-Al Layered Double Hydroxides Films on the Anodized Magnesium Alloy to Improve Corrosion Properties

Comparative Study on Corrosion Resistance of Binary and Ternary Layered Double Hydroxide Films on Magnesium Lithium Alloy

Morphology, Structure and Corrosion Resistance of Mg–Al LDH Films Fabricated in Different Al3+ Concentration Solutions

Preparation and corrosion behavior of Mg(Li)-M layered double hydroxides films on the surface of magnesium-lithium alloy

Effects of Deformation Processes on Morphology, Microstructure and Corrosion Resistance of LDHs Films on Magnesium Alloy AZ31

Fabrication of Superhydrophobic Layered Double Hydroxides Films with Different Metal Cations on Anodized Aluminum 2198 Alloy

Enhanced Corrosion Resistance of Layered Double Hydroxide Films on Mg Alloy: The Key Role of Cationic Surfactant

Characterization and corrosion resistance of a composite layered double hydroxides film on Mg–4Zn alloy in Hank's solution

Fabrication of superhydrophobic layered double hydroxide composites to enhance the corrosion-resistant performances of epoxy coatings on Mg alloy

Step-by-Step In-Situ Preparation of Magnesium-Aluminum Layered Double Hydroxide Film to Improve the Corrosion Resistance of Az31 Magnesium Alloy