Highly Stable Cycling of Amorphous Li2CO3-Coated Alpha-Fe2o3 Nanocrystallines Prepared Via a New Mechanochemical Strategy for Li-Ion Batteries

Yaxiong Yang,Yongfeng Liu,Kaichao Pu,Xing Chen,He Tian,Mingxia Gao,Min Zhu,Hongge Pan

DOI: https://doi.org/10.1002/adfm.201605011

IF: 19

2016-01-01

Advanced Functional Materials

Abstract:In this study, an amorphous Li2CO3-coated nanocrystalline alpha-Fe2O3 hierarchical structure is synthesized for the first time using a facile one-step mechanochemical process at room temperature, taking advantage of the concurrence of repeated fracture-cold welding of material's particles and a gas-solid redox reaction. The conformal coating and hierarchical structure significantly increase the cycling durability and rate capability. Typically, a 1-3 nm thick amorphous Li2CO3 layer is conformally coated on Fe2O3 nanocrystallines (approximate to 10 nm in size) that form hierarchically aggregated particles 400-800 nm in size by ball milling alpha-Fe2O3 with LiH in CO2. The prepared Li2CO3-coated nanocrystalline alpha-Fe2O3 exhibits highly stable long-term cyclability as it delivers a reversible capacity of 975 mAh g(-1) with 99% of retention after 400 cycles at 100 mA g(-1). At a high rate of 3000 mA g(-1), its reversible capacity still remains at 537 mAh g(-1), superior to the uncoated counterpart (311 mAh g(-1)). Moreover, amorphous Li2O and Li2CO3 coatings are also similarly produced on Fe2O3 and NiO nanocrystallines, respectively, representing the general applicability of this mechanochemical approach.