Preparation of nitrogen-doped microporous modified biochar by high temperature CO2–NH3 treatment for CO2 adsorption: effects of temperature

Xiong Zhang,Jing Wu,Haiping Yang,Jingai Shao,Xianhua Wang,Yingquan Chen,Shihong Zhang,Hanping Chen

DOI: https://doi.org/10.1039/c6ra23748g

IF: 4.036

2016-01-01

RSC Advances

Abstract:Nitrogen-rich agricultural waste, soybean straw, was used as a raw material to prepare high efficiency CO2 adsorbents (nitrogen-doped porous modified biochars). Three different modification methods for the preparation of these adsorbents were compared, i.e. activation with carbon dioxide, ammonification with ammonia (NH3) and high temperature treatment with the mixture of CO2 and NH3. Effects of modification temperature on physicochemical properties of the modified biochars and influences of adsorption temperature on their CO2 capture performances were both investigated. Activation with CO2 obviously developed the pore structure of modified biochars, especially micropores, while the ammonification with NH3 and modification with the mixture not only developed porosity, but also introduced nitrogen functional groups, and the modification with the mixture was better than the ammonification with NH3. As the modification temperature increased, the micropore surface area and N/C ratio of the modified biochars by the modification with the mixture both increased first, and reached the maximum at 800 degrees C, and then decreased. Furthermore, at the lower adsorption temperature, the micropore structure played an important role to influence the CO2 capture performance, while at the higher adsorption temperature, the chemical properties, especially the nitrogen functional groups, contributed more to the CO2 capture.