Abstract:In this study, the leaching of zinc from sphalerite in nitric acid (HNO 3 )/hydrogen peroxide (H 2 O 2 ) binary solution was examined via kinetic study. The result showed that the amount of zinc leached increased as the temperature and leachant concentration increased, from 53.8 to 91% for H 2 O 2 concentrations of 2 and 10 M; 53 to 93.2% for temperature of 30 and 90 ° C, respectively, and decreased as the solid/liquid ratio and particle diameter increased from 92.3 to 55.9% for S/L ratios of 20 and 50 g/L; 93.4 to 51.1% for particle diameters of <75 μm and <425 μm, respectively. The solid film diffusion model provided the finest description of the experimental data while chemical reaction was established as the rate-limiting step, with activation energy of 26.52 kJ/mol. Hence, a binary solution of HNO 3 and H 2 O 2 was established as a viable route towards recovering zinc from sphalerite. Le processus de lixiviation hydrométallurgique fait l'objet d'une attention croissante dans la métallurgie extractive en raison de sa rentabilité, de son processus écologique, de son efficacité énergétique ainsi que de sa capacité à traiter des minerais à faible teneur. Dans cette étude, on a examiné la lixiviation du zinc à partir de la sphalérite dans une solution binaire d'acide nitrique (HNO 3 )/peroxyde d'hydrogène (H 2 O 2 ) via une étude cinétique. Les paramètres étudiés comprennent la température de lixiviation, la concentration de lixiviation, le diamètre des particules et le rapport solide/liquide (S/L). Les résultats ont montré que la quantité de zinc lixivié augmentait à mesure que la température et la concentration de lixiviation augmentaient, de 53.8 à 91% pour des concentrations de H 2 ē 2 de 2 et 10 M; 53 à 93.2% pour des températures de 30 et 90°C, respectivement, et diminuait à mesure que le rapport solide/liquide et le diamètre des particules augmentaient de 92.3 à 55.9% pour des rapports S/L de 20 et 50 g/L; 93.4 à 51.1% pour des diamètres de particules de <75 μm et <425 μm, respectivement. Le modèle de diffusion du film solide a fourni la description la plus fine des données expérimentales tandis que la réaction chimique a été établie comme étape cinétiquement limitante, avec une énergie d'activation de 26.52 kJ/mol. Les résultats de XRD des résidus de post-lixiviation ont révélé les phases minérales présentes sous forme de gahnite, de soufre, de fluorite, de quartz et de sylvite. Par conséquent, on a établi une solution binaire de HNO 3 et de H 2 O 2 comme une route viable pour récupérer le zinc de la sphalérite.

Selective and Efficient Extraction of Zinc from Mixed Sulfide–oxide Zinc and Lead Ore

Efficient separation of zinc from zinc containing copper sulfide concentrate by chemical leaching

Selective Lead Extraction from Zinc Calcine and Zinc Leaching Residue by Leaching with Monoethanolamine Solvent Systems

Ammonia Leaching of Zinc from Low-grade Oxide Zinc Ores Using the Enhancement of the Microwave Irradiation

The influence of chalcopyrite, galena and pyrite on the selective extraction of zinc from base metal sulphide concentrates

Reductive leaching of indium and zinc from zinc neutral leach residue with sulphuric acid and sulphur dioxide

Enhanced Recovery of Zn from Carbonate-Type Mixed Oxidized Ore (CMO) by Combining Organic Acid Leaching with Mechanical Activation

Mechanism Analysis and Experimental Research on Leaching Zn from Zinc Oxide Dust with an Ultrasound-Enhanced NH3-NH4Cl-H2O System

Selective extraction performance of Ni, Cu, Co, and Mn adopted by a coupled leaching of low-grade Ni-sulfide ore and polymetallic Mn-oxide ore in sulphuric acid solutions

A Study on the Mechanism and Kinetics of Ultrasound-Enhanced Sulfuric Acid Leaching for Zinc Extraction from Zinc Oxide Dust

Effective separation of Zn, Fe, and Mn from roasting-water leaching solution of blast-furnace dust using a precipitation-solvent extraction process

Leaching of lead from sphalerite concentrate direct leaching residue by hydrochloric acid and sodium chloride for preparation of lead oxides

Phase Transformation Analysis and Process Optimisation of Low-Grade Lead–Zinc Oxysulphide Ore Carbothermal Reduction

Leaching kinetics of copper and valuable metal extraction from copper-cadmium residues of zinc hydrometallurgy by oxidation acid leaching

Hydrometallurgical Process for Zinc Recovery from C.Z.O. Generated by the Steelmaking Industry with Ammonia–Ammonium Chloride Solution

Extraction of Lead and Zinc from a Rotary Kiln Oxidizing Roasting Cinder

Kinetics of sphalerite dissolution for potential zinc recovery via oxidative leaching

Simultaneous dissolution of nickel, copper and cobalt from low grade nickel matte by (NH4)2S2O8-H2SO4 oxidative leaching

Selective extraction and recovery of tin from hazardous zinc-leaching residue by oxalic acid/sulfuric acid mixture leaching and hydrolytic precipitation

A Novel Technology for Separating Copper, Lead and Zinc in Flotation Concentrate by Oxidizing Roasting and Leaching

Study on Beneficiation of A Refractory Low Grade Oxidized Zinc Ore