The Flow Behavior and Microstructure Evolution During (α + Β) Deformation of Β Wrought TA15 Titanium Alloy

A. M. Zhao,H. Yang,X. G. Fan,P. F. Gao,R. Zuo,M. Meng

DOI: https://doi.org/10.1016/j.matdes.2016.07.001

IF: 9.417

2016-01-01

Materials & Design

Abstract:The hot compressions in (α+β) region were conducted on β wrought TA15 titanium alloy, so as to investigate the effect of β working on the flow behavior and dynamic globularization of lamellar microstructure. The results indicated that initial β grain size had no significant influence on flow stress. The dynamic globularization rate of α laths in smaller β grains was higher due to the difference in lamellar length. β predeformation would decrease the flow stress of (α+β) deformation. Most of α laths in the microstructure after β predeformation were short with a geometric orientation vertical to β grain boundary and rotated together during compression, which would promote the formation of α/α substructures, thus highly enhanced the dynamic globularization rate of α laths. While β heat treated microstructure had long α lamellae with a random orientation, which tended to become kinked first and then break up into short ones, resulting in the delay of dynamic globularization. In addition, prior β deformation changed the initial α phase texture and dynamic globularization rate would be affected by strain path. When the compressive direction in (α+β) region was vertical to that of β predeformation, the globularized fraction of α lamellae was apparently high.