Abstract:Magnetic Fe3O4/P (MMA/DVB)((core))-P (St/(GMA/DVB)((shell)) composite microspheres with core-shell structure were prepared by a two-step method. (1) Preparation of the magnetic cores: First, the magnetic miniemulsion composed of organic ferrofluid droplets dispersed in water was obtained by rapid addition of an oil-based magnetite ferrofluid, with a solid content 60 wt%, into the aqueous solution using DNS-86 (polymerizable surfactant) as surfactant in the condition of ultrasonic emulsification. Then, the copolymerization monomers of methyl mathacrylate (MMA) and divinyl benzene (DVB) were injected directly into the magnetic miniemulsion. Because of their hydrophobic character, once the monomers were added into the emulsion, the methyl mathacrylate (MMA) and divinyl benzene (DVB) would have a high tendency to diffuse inside the organic phase of the ferrofluid droplets to form monomer swelling magnetic miniemulsion, Which were supposed to be the main locus for copolymerization. in succession, the temperature was rapidly increased to 70 degrees C and starting the miniemulsion copolymerization to form uniform magnetic latexes. (2) Preparation of the core/shell hybrid polymeric microspheres: Through varying the feeding amount of styrene (St), glycidyl methacrylate (GMA) and DVB, the core-shell structured microspheres were rationally fabricated by the seed emulsion copolymerization using the above magnetic latex as the core emulsion. This preparation process is convenient and effective. Extensive. characterization by X-ray diffraction (XRD), high resolution transmission electron microscopy (HR-TEM), thermogravimetric analysis (TGA) and vibrating sample magnetometer (VSM) showed that the magnetite content of Fe3O4/P(MMA/DVB) composite microspheres was 84 wt %. The magnetite content of the magnetic composite microspheres with core-shell Structure is varied from 20 wt % to 76 wt % by feeding different amount of monomers. The average diameter of the magnetic seeded microspheres and the core-shell composite microspheres is 150 nm and 350 nm, respectively. The functional epoxy groups on the surface of the core-shell composite microspheres can be further modified to load biomolecules.

The Latest Developments of Magnetic Composite Microspheres

Progress in polymer bonded magnetic composites

Research Progress of Magnetic Fluids

Research Progress in Magnetic Polymeric Microspheres

Recent research progress on the preparation and application of magnetic nanospheres

Research Progress in Preparation Techniques of Functional Magnetic Polymer Microsphere

Progress in Preparation and Application of Magnetic Mesoporous Carbon Composites

Preparation and Application of Magnetic Microsphere Carriers

Recent progress in magnetic nanoparticles: synthesis, properties, and applications

In-situ Microwave Characterization of Ferromagnetic Microwires-Filled Polymer Composites: A Mini Review

Magnetic Microsphere and Its Use in Biochemical Separation and Analysis

Ferromagnetic microwires enabled multifunctional composite materials

Preparation and Applications of Magnetic Mesoporous Silica

Co-Based Magnetic Microwire and Field-Tunable Multifunctional Macro-Composites

PREPARATION AND CHARACTERIZATION OF MAGNETIC COMPOSITE MICROSPHERES WITH CORE-SHELL STRUCTURE

Controllable Synthesis and Performance of Magnetic Nanocomposites with Core/shell Structure

Applications of Biology & Medicine on Magnetic Polymer Microsphere

Multi-Functional Thermosensitive Composite Microspheres with High Magnetic Susceptibility Based on Magnetite Colloidal Nanoparticle Clusters

Magnetic metal nanoparticles and their exchange-coupled nanocomposites: chemical synthesis and magnetic properties

Magnetic Colloidal Supraparticles: Design, Fabrication and Biomedical Applications

Synthesis and characterization of magnetic Fe3O4-silica-poly(γ-benzyl-l-glutamate) composite microspheres