Microstructures and Growth Mechanisms of the Polycrystalline CaBaCo2 O5+δ Thin Films Grown on (001)laalo3 Substrates

LI Jun-chi,CHEN Jiang-hua,DING Ying,MA Chun-rui,CHEN Chong-lin,FANG Jing-yue,ZHANG Xue-ao
DOI: https://doi.org/10.3969/j.issn.1001-9731.2014.17.010
2014-01-01
Journal of Functional Biomaterials
Abstract:CaBaCo2 O 5 +δ thin films were deposited on (001 )LaAlO 3 substrates by pulsed laser deposition.The microstructures of the film and substrate were studied by X-ray diffraction (XRD)and of transmission electron microscopy (TEM).Results show that (1 )dislocations and twins appear in the LaAlO 3 substrates,and the (100)wedge-shaped twin was the main type;(2)CaBaCo2 O 5 +δ thin film was polycrystalline in nature,and the initial grain structure with a grain size of about 5-8 nm during growth was kept at the bottom of the film.While the grain size at the top of the film was larger,about 1 1-1 6 nm.Based on the observation results,a growth mechanism of the film was proposed.Possible processes to improve the film quality have also been discussed.
What problem does this paper attempt to address?