Corrosion Behavior of Spiral Welded X60 Pipes in Wet H2S Environment

冯耀荣,李铁虎,李国兴,霍春勇,颜峰

DOI: https://doi.org/10.3321/j.issn:0253-360x.2002.05.021

2002-01-01

Abstract:The H 2S corrosion behavior of over bending and under bending formed spiral submerged arc welded steel pipes in NACE solution has been investigated by use of the self designed full scale pipe corrosion test unit.Results indicate that the H 2S damage of welded pipes shows blister and stress corrosion cracking(SCC) in pipe surface.The H 2S corrosion trend increases with the increase of applying stress and residual stress.The damage mechanism of the welded pipes in H 2S containing solution under the presence of applying stress and residual stress has not only hydrogen induced cracking(HIC),but also stress corrosion cracking,and the applying stress and residual stress promote not only stress corrosion cracking,but also hydrogen induced cracking.The test results reveal that improving pipe surface quality especially weld surface quality,lowering tensile residual stress and controling operating stress are the key measures for controlling the wet H 2S corrosion of welded steel pipes.