Grain Refining Performance of Al–Ti(C 0.7 , N 0.3 ) Master Alloy and Its Effect on Mechanical Properties for Commercial Pure Aluminium

Xuguang An,Ying Liu,Jinwen Ye,Linzhi Wang

DOI: https://doi.org/10.1049/mnl.2016.0048

2016-01-01

Micro & Nano Letters

Abstract:A new Al-4.2 wt.% Ti(C-0.7, N-0.3) master alloy with a uniform microstructure was successfully prepared by casting method. Grain refining test indicates that Al-4.2 wt.% Ti(C-0.7, N-0.3) master alloy exhibits an excellent grain refining performance on commercial pure aluminium and the average grain size of pure Al can be effectively refined to 130 mu m from about 3000 mu m after adding 0.1 wt.% Ti(C-0.7, N-0.3) particles by Al-4.2 wt.% Ti(C-0.7, N-0.3) master alloy. The tensile strength and elongation are increased by about 20.5% from 55 to 66.3 and 14.9% from 39 to 44.8 due to the grain refinement by adding Al-4.2 wt.% Ti(C-0.7, N-0.3) master alloy. Compared with Al-5Ti-1B master alloy, Al-4.2 wt.% Ti(C-0.7, N-0.3) master alloy has a slightly better ability in improving the mechanical properties of pure aluminium due to the better grain refining performance.