Abstract:Lead-free 0.94(Na0.5Bi0.5)TiO3–0.06BaTiO3 (BNT–BT) piezoelectric thick films were fabricated by a tape casting method. The structural and electrical properties of BNT–BT thick films sintered at different temperatures from 1100°C to 1180°C were studied systematically. The X-ray diffraction result showed that all the thick films exhibited a perovskite phase. The increase of grain size of BNT–BT thick films could be observed clearly with increasing sintering temperature from SEM morphologies. It was found that with increasing sintering temperature, the roughness of the films increased from 139nm to 285nm, while the piezoelectric coefficient d33 of the thick films increased monotonically in the range of 1100–1160°C, and then decreased at 1180°C. The maximum value of the piezoelectric coefficient d33 was 112 pC/N at 1160°C. At this sintering temperature, the dielectric constant and loss tangent were 1928 and 5.29% at 1kHz, while the values of the remnant polarization and the coercive field were 26.3μC/cm2 and 27.1kV/cm, respectively. The piezoresponse force microscopy was used to study the piezoelectric behaviors of BNT–BT thick films, which revealed both single domain and layered multi-domain in the grains.

Effects of Heat‐Treatment Temperature on the Properties of (1–x)(na0.5bi0.5)tio3–xbialo3 Lead‐Free Piezoelectric Thin Films

Preparation and Electrical Properties of (1−x)(na0.5bi0.5)tio3–xbialo3 Thin Films by a Sol–gel Process

Sol–gel Synthesis of 0.94(bi0.5na0.5)tio3–0.06batio3 Lead-Free Piezoelectric Films: Effect of Pyrolysis Temperature on Phase Evolution and Electrical Properties

Preparation and electric properties of Bi0.5Na 0.5TiO3-Bi(Al0.5Ga0.5)O3 lead-free piezoceramics

Structural, Dielectric and Piezoelectric Properties of (bi0.5na0.5)tio3–(bi0.5k0.5)tio3–bi(zn0.5ti0.5)o3 Thin Films Prepared by Sol–gel Method

Piezoelectric Properties in (K0.5bi0.5)tio3-(Na0.5bi0.5)tio3-batio3 Lead-Free Ceramics

Structure and electrical properties of (Bi0.5Na 0.5)0.94Ba0.06TiO3-Bi 0.5(Na0.82K0.18)0.5TiO 3-BiAlO3 lead free piezoelectric ceramics

Temperature and Composition Dependent Phase Transitions of Lead-Free Piezoelectric (Bi0.5na0.5)tio3-Batio3 Thin Films.

Piezoelectric properties in (K0.5Bi0.5)TiO3-(Na0.5Bi0.5)TiO3-BaTiO3 lead-free ceramics.

Textured Bi1/2Na1/2TiO3‐BaTiO3 Lead‐Free Films with Enhanced Piezoelectric Property and Depolarization Temperature

Large piezoelectric properties of (1 − x)Na 0.5 Bi 0.5 TiO 3 –xBaTiO 3 thin films prepared by sol–gel method

Structure and Electrical Properties of (1 − X )(na 0.5 Bi 0.5 ) 0.94 Ba 0.06 TiO 3 – X SmAlO 3 Lead-Free Piezoelectric Ceramics

Effect of Sintering Temperature on Structural and Electrical Properties of Lead-Free BNT–BT Piezoelectric Thick Films

Preparation and electric properties of Bi0.5 Na0.5 TiO3- Bi (Mg0.5 Ti0.5) O3 lead-free piezoceramics

Piezoelectric and Dielectric Properties of (bi0.5na0.5)0.94ba0.06tio3–ba(zr0.04ti0.96)o3 Lead-Free Piezoelectric Ceramics

Piezoelectric Properties of Lead-Free (na0.5bi0.5)(0.95)ba0.05tio3 Thin Films on Polycrystalline Nickel Foils

Annealing Temperature Dependence of Effective Piezoelectric Coefficients for Bi3.15eu0.85ti3o12 Thin Films

Morphotropic Phase Boundary and Electrical Properties in (1−x)bi0.5na0.5tio3−xbi(zn0.5ti0.5)o3 Lead-Free Piezoceramics

Preparation and electrical properties of the new lead-free (1 − <i>x</i>)Bi<sub>0.5</sub>Na<sub>0.5</sub>TiO<sub>3</sub>–<i>x</i>Ba(Ni<sub>1/3</sub>Nb<sub>2/3</sub>)O<sub>3</sub> piezoelectric ceramics

Structure and Electrical Properties of (1−x) (bi0.5 (na0.82k0.18)0.5) TiO3–x BiAlO3 Lead-Free Piezoelectric Ceramics

Piezoelectric and Dielectric Properties of Bi0˙5(Na0˙84K0˙16)0˙5TiO3–Ba(Zr0˙04Ti0˙96)O3lead Free Piezoelectric Ceramics