Abstract:Polydimethylsiloxane (PDMS) is usually used to obtain favorable performances of waterborne polyurethane (WPU) such as higher hardness, exceptional thermal stability and lower interfacial tension. However, there is always a problem that waterborne polyurethane (WPU) often performs weak tensile strength, lower tenacity and brittle property at room temperature when polydimethylsiloxane (PDMS) is embedded into the backbone of polyurethane. The study aims to address the problem by constructing dual crosslinking structure, namely introducing trimethylolpropane as an intramolecular crosslinking agent into prepolymers and then adding waterborne polycarbodiimide (SK-400) as a post-crosslinking agent in order to further enlarge the degree of crosslinking and mainly make up for the shortcoming that mechanical property decreases when polydimethylsiloxane (PDMS) was inserted into molecule chains. Initially a novel inner-crosslinking prepolymer (SiWPU) comprising polydimethylsiloxane need to be synthesized successfully by inserting trimethylolpropane into prepolymers. Then the sample SiWPU-3 was picked out as a matrix resin and dropwise added polycarbodiimide (SK-400) as a post-crosslinking agent into the matrix resin (C–SiWPU). As pH was gradually lowering following the evaporation of triethylamine in the emulsion (C–SiWPU), carboxyl groups (COOH) in prepolymers started to react with SK-400 (NCN) to form twofold crosslinking structure. When 0%, 2%, 4%, 6%, and 8 wt% of waterborne polycarbodiimide (SK-400) was incorporated into the solution, the tensile strengths are 47.8 MPa, 57.7 MPa, 65 MPa, 57.6 MPa and 54.5 MPa and the elongation at break 732%, 756%, 798%, 707% and 700%. The crosslinking density of SiWPU-3 without the addition of waterborne polycarbodiimide (SK-400) is 3.86 × 10−3 mol/cm3. As 6 wt% of waterborne polycarbodiimide (SK-400) was added into the emulsion of SiWPU-3, the crosslinking density of C–SiWPU-6 (6 wt% SK-400) is 6.19 × 10−3 mol/cm3. The films show excellent extensibility and exceptional tenacity. Hence, the emulsion is able to be applied in leather industry.

In Situ Incorporation Of Diamino Silane Group Into Waterborne Polyurethane For Enhancing Surface Hydrophobicity Of Coating

Synthesis and Surface Properties of Waterborne Polyurethane Modified by Polysiloxane

Synthesis of waterborne polyurethane containing alkoxysilane side groups and the properties of the hybrid coating films

Synergistic modification of short‐chain fluoro‐alcohol and siloxane end‐capping agents endowing an enhanced superhydrophobic waterborne polyurethane coating

Synthesis and Characterization of Self-matting Waterborne Polyurethane Emulsion Modified by Silane Coupling Agent

Synthesis and Characterization of Polyorganosiloxane Modified Waterborne Polyurethane

Preparation and Properties of Waterborne Polyurethane/nanosilica Composites: A Diol As Extender with Triethoxysilane Group

Synthesis of Waterborne Polyurethane Modified by Nano-SiO2 Silicone and Properties of the WPU Coated RDX

Preparation and Properties of Hydrophobic Polyurethane Based on Silane Modification

Effects of aminopropyl-terminated polydimethylsiloxane on structure and properties of waterborne polyurethane-acrylate

Improving water resistance of waterborne polyurethane coating with high transparency and good mechanical properties

Synthesis and characterization of waterborne polyurethanes with alkoxy silane groups in the side chains for potential application in waterborne ink

Synthesis and Properties of Intermolecular Self-crosslinking Organic-inorganic Hybrid Waterborne Polyurethane Based on CuAAC Reaction

Preparation and Application of UV Curable Waterborne Organosilicon Acrylic Polyurethane with Controllable Silicon Content

Preparation and properties of waterborne siloxane-containing polyurethane for moisture permeable textile coating

Dihydroxypropyl-Terminated Polysiloxane Modified Uv Cure Water-Borne Polyurethane

Preparation and Properties of Waterborne Polyurethane with PDMS Side Chain

Synthesis of waterborne polyurethane by inserting polydimethylsiloxane and constructing dual crosslinking for obtaining the superior performance of waterborne coatings

Polydimethylsiloxane containing waterborne hydrophobic polyurethane coatings with good adhesion to metals: Synthesis and characterization

Synthesis, Characterization and Surface Properties of Cross-linked Polyurethane Dispersion Modified by Organosiloxane

Synthesis and Properties of Waterborne Polyurethane Modified with Dihydroxylalkyl-Terminated Polydimethylsiloxane