Abstract:One of the useful features of 3D-printed specimens of recycled polyethylene terephthalate glycol (R-PETG) is the ability to repetitively develop free recovery as well as the work-generating, shape-memory effect. This behavior is enabled by the R-PETG's capacity to stiffen during cooling, thus allowing for a new temporary shape to be induced. Aiming to devise an explanation for the polymer's stiffening, in this study, the variation in some of the R-PETG's parameters during cooling are emphasized and discussed. The evolution of an R-PETG filament's shape was monitored during room-temperature-bending heating-cooling cycles. Straight-shape recovery and the complete loss of stiffness were observed at the start and the end of heating, respectively, followed by the forced straightening of the filament, performed by the operator, around 40 °C, during cooling. The tests performed by dynamic mechanical analysis disclosed the rise of the storage modulus (E') after 100 °C heating followed by either liquid-nitrogen- or air-cooling to room temperature, in such a way that E' was always larger after cooling than initially. Static tests emphasized a peculiar stress variation during a heating-cooling cycle applied in air, within the heating chamber of the tensile testing machine. Tensile-failure tests were performed at -10 °C at a rate of 100 mm/min, with specimens printed at various deposition directions between 10 and 40° to the transversal direction. The specimens printed at 40°, which had the largest ultimate strains, were broken with tensile rates between 100 and 500 mm/min. Deformation rate increase favored the shift from crazing to delamination failure modes. The correlation between the structural changes, the sharp E' increase on heating, and the stiffening induced by cooling represents a novel approach that enables the use of 3D-printed R-PETG for the fabrication of the active parts of low-priced lightweight resettable actuators.

Recycled PET Packaging Materials of Improved Toughness— Importance of Devitrification of the Rigid Amorphous Fraction

Optimizing Physical Aging in Poly(ethylene Terephthalate)-Glycol (PETG)

Effects of Physical Aging on Thermomechanical Behaviors of Poly(ethylene Terephthalate)-Glycol (PETG)

Recyclability of elastomer toughened recycled poly(ethylene terephthalate): The effect of grinding-extrusion-injection moulding on the mechanical and morphological properties of the blend

Effect of rPET Content and Preform Heating/Cooling Conditions in the Stretch Blow Molding Process on Microcavitation and Solid-State Post-Condensation of vPET-rPET Blend: Part I—Research Methodology and Results

Upcycling discarded polyethylene terephthalate plastics into superior tensile strength and impact resistance materials with a facile one–pot process

Biocatalytic Degradation Efficiency of Postconsumer Polyethylene Terephthalate Packaging Determined by Their Polymer Microstructures

Mechanically strong and heat-resistant waste poly (ethylene terephthalate) derived by carbon dioxide treatment at ambient temperature

Influence of Different Molecular Weights and Concentrations of Poly(glycidyl methacrylate) on Recycled Poly(ethylene terephthalate): A Thermal, Mechanical, and Rheological Study

A Review on the Formulation and Rupture Properties of Polyethylene Terephthalate in a Mechanical Recycling Context

Preparation of High‐modulus and High‐strength Poly(ethylene Terephthalate) Film by Zone‐annealing Method

Atomic insights into the thermal degradation of polyethylene terephthalate combining STA-FTIR and DFT methods

Variations in the Thermomechanical and Structural Properties during the Cooling of Shape-Memory R-PETG

Recycled Poly(Ethylene Terephthalate) from Waste Textiles with Improved Thermal and Rheological Properties by Chain Extension

Evaluation of PET recyclability and characterization of modified reprocessed‐PET for industrial application

Achieving bottle‐grade poly(ethylene terephthalate)‐like properties from blends of bottle‐grade and thermoform‐grade poly(ethylene terephthalate)

UV Pretreatment Impairs the Enzymatic Degradation of Polyethylene Terephthalate

Influence of plastic recycling—a feasibility study for additive manufacturing using glycol modified polyethylene terephthalate (PETG)

Film Blowing of Linear and Long-Chain Branched Poly(ethylene terephthalate)

DMA Investigation of the Factors Influencing the Glass Transition in 3D Printed Specimens of Shape Memory Recycled PET

Thermal degradation evaluation of polyethylene terephthalate microplastics: Insights from kinetics and machine learning algorithms using non-isoconversional TGA data