A-site deficient La 0.52 Sr 0.28 Ti 0.94 Ni 0.06 O 3 by low-pulsed electric current treatment: achieved exsolution of B-site Ni nanoparticles and significant improvement of electrocatalytic properties

Wenwen Yu,Jingang Qi,Xin Hu,Sifan Qiao,Jian Shang,Liang Liu,Bing Wang,Lidan Tang,Wei Zhang,Yu Cheng

DOI: https://doi.org/10.1088/1361-6528/ac64ac

IF: 3.5

2022-04-22

Nanotechnology

Abstract:Abstract Perovskite materials with exsolved nanoparticles have a wide range of applications in energy conversion systems owing to their unique basal plane active sites and excellent catalytic properties. The introduction of A-site deficiency can help the formation of highly mobile oxygen vacancies and remarkably enhance the reducibility of Ni nanoparticles, thus significantly increasing electronic conductivity and catalytic activity simultaneously. Herein, we adopt pulsed electric current (PEC) treatment, a novel approach instead of the long-time high-temperature reduction technique, and for the first time review that the exsolution of minuscule Ni nanoparticles (8–20 nm) could be facilitated on Ni-doped La 0.52 Sr 0.28 Ti 0.94 Ni 0.06 O 3 (LSTN) anodes with A-site deficiency. Encouragingly, finding that low PEC can successfully lead to nanoparticle exsolution and show a significantly improved oxygen evolution reaction performance of LSTN-PEC (LSTN after PEC treatment) possessing A-site deficiency, the onset potential of LSTN-PEC (500 V) (LSTN after PEC treatment with 500 V–4 Hz–90 s) was advanced by 0.173 V, the R ct value was reduced by 82.38 Ω·cm 2 , and the overpotential was also reduced by 73 mV.

materials science, multidisciplinary,physics, applied,nanoscience & nanotechnology