Simultaneous Enhancement of Interfacial Stability and Kinetics of Single-Crystal LiNi 0.6 Mn 0.2 Co 0.2 O 2 through Optimized Surface Coating and Doping
Wenda Bao,Guannan Qian,Lianqi Zhao,Yi Yu,Longxing Su,Xincan Cai,Haojie Zhao,Yuqing Zuo,Yue Zhang,Haoyuan Li,Zijian Peng,Linsen Li,Jin Xie
DOI: https://doi.org/10.1021/acs.nanolett.0c03778
IF: 10.8
2020-11-25
Nano Letters
Abstract:Balancing interfacial stability and Li<sup>+</sup> transfer kinetics through surface engineering is a key challenge in developing high-performance battery materials. Although conformal coating enabled by atomic layer deposition (ALD) has shown great promise in controlling impedance increase upon cycling by minimizing side reactions at the electrode–electrolyte interface, the coating layer itself usually exhibits poor Li<sup>+</sup> conductivity and impedes surface charge transfer. In this work, we have shown that by carefully controlling postannealing temperature of an ultrathin ZrO<sub>2</sub> film prepared by ALD, Zr<sup>4+</sup> surface doping could be achieved for Ni-rich layered oxides to accelerate the charge transfer yet provide sufficient protection. Using single-crystal LiNi<sub>0.6</sub>Mn<sub>0.2</sub>Co<sub>0.2</sub>O<sub>2</sub> as a model material, we have shown that surface Zr<sup>4+</sup> doping combined with ZrO<sub>2</sub> coating can enhance both the cycle performance and rate capability during high-voltage operation. Surface doping via controllable postannealing of ALD surface coating layer reveals an attractive path toward developing stable and Li<sup>+</sup>-conductive interfaces for single-crystal battery materials.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.nanolett.0c03778?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.nanolett.0c03778</a>.Quasi <i>in situ</i> X-ray photoelectron spectroscopy (XPS) characterizations of Zr 3d and Ni 2p (Figure S1), XPS characterizations of O 1s (Figure S2), energy-dispersive spectroscopy (EDS) mapping of 50-ZrO<sub>2</sub>-700 °C-NCM (Figure S3), cross-sectional scanning electron microscopy (SEM) images of SC-NCM and 5-ZrO<sub>2</sub>-NCM electrode collected after 50 cycles (Figure S4), reproducible cycle and rate performance of 5-ZrO<sub>2</sub>-500 °C-NCM (Figure S5), XPS characterizations of F 1s (Figure S6), SEM characterizations of SC-NCM; 5-ZrO<sub>2</sub>-NCM; 5-ZrO<sub>2</sub>-500 °C-NCM; 5-ZrO<sub>2</sub>-700 °C-NCM after 50 cycles (Figure S7), cycle stability of NCM cathodes at 1 C (180 mA/g) in this study compared to literature reports (Table S1) (<a class="ext-link" href="/doi/suppl/10.1021/acs.nanolett.0c03778/suppl_file/nl0c03778_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology