Removal of chlorobenzene over LaMnO3 and OMS-2 catalysts in a dielectric barrier discharge reactor
Liying Jiang,Zhiwei Yao,Pengju Wang,Jianmeng Chen,Yufen Zhang,Wu Huang,Xiang Cao,Yufeng Xu
DOI: https://doi.org/10.1016/j.jece.2021.105898
IF: 7.7
2021-10-01
Journal of Environmental Chemical Engineering
Abstract:<p>Plasma-catalytic removal of chlorobenzene (CB) was conducted in a dielectric barrier discharge (DBD) reactor over two manganese-based catalysts, LaMnO<sub>3</sub> and cryptomelane-type octahedral molecular sieve (OMS-2). The physicochemical properties of two catalysts were characterized by XRD, SEM, TEM, BET, XPS and H<sub>2</sub>-TPR. It was shown that OMS-2 catalyst had larger surface area, smaller particle size, better redox properties, higher ratio of Mn<sup>4+</sup>/Mn<sup>3+</sup> and higher content of surface-adsorbed oxygen (O<sub>ads</sub>). The introduction of manganese-based catalysts enhanced CB removal, increased the CO<sub>2</sub> selectivity, and inhibited ozone (O<sub>3</sub>) and NO<sub><em>x</em></sub> formation. OMS-2 exhibited a better degradation, mineralization and energy yield, with 89.5% of CB degradation, 57.6% of CO<sub>2</sub> selectivity and 0.54 g kWh<sup>−1</sup> at discharge voltage of 6 kV, than LaMnO<sub>3</sub> in the NTP-catalytic reactor and this was ascribed to more active sites, more O<sub>ads</sub>, higher redox property and better O<sub>3</sub> decomposition ability on OMS catalyst surface. The two manganese-based catalysts were stable in the NTP-catalysis system although some intermediate byproducts were deposited on the catalyst surface during the 24-h activity cycling tests. Moreover, the intermediate byproducts were analyzed by GC/MS, and then the possible degradation pathways of CB decomposition in the plasma-catalysis system were suggested.</p>
engineering, chemical, environmental