Abstract:Ordered mesoporous carbon (OMC) supported well-dispersed PtFex nanoparticles with a controllable size distribution were prepared via a modified polyol synthesis route, using hexachloroplatinic acid and ferric chloride as Pt and Fe source, and ethylene glycol as a reducing agent. The catalytic activities relevant to direct methanol fuel cell of the PtFex/OMC composites were investigated using cyclic voltammetry, single-cell proton exchange membrane fuel cell (PEMFC) test and electrochemical impedance spectroscopy (EIS) technique. Due to the existence of more Pt0 species and Fe ion corrosion caused by the formation of the alloyed PtFex catalyst, Pt0 can provide the more active sites for methanol oxidation reaction, and the methanol oxidation activity of the PtFex/OMC electrode is evidenced to be enhanced by the increased anodic peak current with increasing the incorporation content of Fe. The oxygen reduction reaction (ORR) current density of 0.662 A cm−2 and power density of 237.2 mW cm−2 generated by the PtFe3/OMC sample are more than two times the values of 0.32 mA cm−2 and 102.6 mW cm−2 by the Pt/OMC sample. The PtFe3/OMC catalyst in 0.5 M H2SO4 + 1 M CH3OH displays the highest specific catalytic activity of 100.6 mA m−2, which is almost 3 times lower than that of 283.7 mA m−2 in 0.5 M H2SO4. The enhanced higher activity for the PtFe3/OMC sample can be firstly attributed to a highly homogeneous dispersion of the PtFe3 nanoparticles on the mesoporous channels within OMC, such PtFe3 nanoparticles with a diameter of 3.3 nm can accelerate the formation of Pt–OH groups. Meanwhile, the alloyed PtFe3 nanoparticles can provide a lower onset potential for the electrooxidation of CO/H2 than that of pure Pt, and would contribute more to the promotion of C–H breaking and COad tolerance. Furthermore, the larger surface area, the favorable pore structure and the structural integrity between the PtFe3 nanoparticles and the OMC matrix, will effectively facilitate the transportation of reactants and products in liquid electrochemical reactions.

Application of Pt-Co Nanoparticles Supported on CeO2-C As Electrocatalyst for Direct Methanol Fuel Cell

Highly Active Nanoporous Pt-based Alloy As Anode and Cathode Catalyst for Direct Methanol Fuel Cells

Electro-catalytic activity of enhanced CO tolerant cerium-promoted Pt/C catalyst for PEM fuel cell anode

Highly Active Carbon-Supported Pt Nanoparticles Modified and Dealloyed with Co for the Oxygen Reduction Reaction

Pt-Co Supported On Polypyrrole-Multiwalled Carbon Nanotubes As An Anode Catalyst For Direct Methanol Fuel Cells

Efficient Synthesis of Pt–Co Nanowires As Cathode Catalysts for Proton Exchange Membrane Fuel Cells

MnO2/CNT supported Pt and PtRu nanocatalysts for direct methanol fuel cells.

Mesoporous CeO2–C hybrid spheres as efficient support for platinum nanoparticles towards methanol electrocatalytic oxidation

Mixed‐Dimensional Pt–Ni Alloy Polyhedral Nanochains As Bifunctional Electrocatalysts for Direct Methanol Fuel Cells

Nano-structured Carbon Support for Pt/C Anode Catalyst in Direct Methanol Fuel Cell

Mixed‐Dimensional Pt‐Ni Alloy Polyhedral Nanochains As Bifunctional Electrocatalysts for Direct Methanol Fuel Cell

Direct Synthesis of Bimetallic PtCo Mesoporous Nanospheres As Efficient Bifunctional Electrocatalysts for Both Oxygen Reduction Reaction and Methanol Oxidation Reaction.

3D Porous N/S Co-Doped Carbon Nanosheets Derived from Ionic Liquids As Efficient Electrocatalysts for Direct Methanol Fuel Cells

Highly Dispersed Pd-CeO2 Nanoparticles Supported on N-Doped Core–Shell Structured Mesoporous Carbon for Methanol Oxidation in Alkaline Media

Self-standing CoFe Embedded Nitrogen-Doped Carbon Nanotubes with Pt Deposition Through Direct Current Plasma Magnetron Sputtering for Direct Methanol Fuel Cells Applications

Direct methanol fuel cell with enhanced oxygen reduction performance enabled by CoFe alloys embedded into N -doped carbon nanofiber and bamboo-like carbon nanotube

Application of N-doped carbon nanotube-supported Pt-Ru as electrocatalyst layer in passive direct methanol fuel cell

Exploiting the Synergistic Electronic Interaction between Pt-Skin Wrapped Intermetallic PtCo Nanoparticles and Co-N-C Support for Efficient ORR/EOR Electrocatalysis in a Direct Ethanol Fuel Cell

Well-dispersed and Size-Tuned Bimetallic PtFex Nanoparticle Catalysts Supported on Ordered Mesoporous Carbon for Enhanced Electrocatalytic Activity in Direct Methanol Fuel Cells

A Novel Co-Precipitation Method for Preparation of Pt-CeO2 Composites on Multi-Walled Carbon Nanotubes for Direct Methanol Fuel Cells

A Novel Nanocomposite Catalytic Cathode for Direct Methanol Fuel Cells