Dy 3+ Doped Ca 9 Gd(PO 4 ) 7 : a novel single-phase full-color emitting phosphor

Lurong Yang,Zhongfei Mu,Shaoan Zhang,Qiang Wang,Daoyun Zhu,Yu Zhao,Dongxiang Luo,Qingtian Zhang,Fugen Wu

DOI: https://doi.org/10.1007/s10854-018-8638-7

2018-01-01

Abstract:A series of un-doped and Dy 3+ doped Ca 9 Gd(PO 4 ) 7 phosphors were synthesized by traditional solid state reactions. X-ray diffraction analysis and scanning electronic microscope observation were carried out to examine the phase formation and morphology of prepared samples. Emission spectra under the excitation at 350 nm ultraviolet light turn out that main emission bands are located at 480, 570 and 659 nm, which can be assigned to the optical transitions 4 F 9/2 → 6 H 15/2 , 4 F 9/2 → 6 H 13/2 and 4 F 9/2 → 6 H 11/2 of Dy 3+ , respectively. Comparison of emission spectra upon excitation of 273 nm between un-doped and Dy 3+ doped Ca 9 Gd(PO 4 ) 7 samples proves that effective energy transfer from Gd 3+ to Dy 3+ takes place. The Commission International de I’Eclairage color coordinates (0.272, 0.322) located in white region was achieved. With the increasing doping concentration of Dy 3+ , concentration quenching is clearly observed and the optimum content of doped Dy 3+ is 0.12. The mechanism of concentration quenching is experimentally ascertained to be electric dipole–dipole interactions. The study of quantum efficiency and thermal stability shows that our phosphors have higher quantum efficiency and better thermal stability. This work indicates that our phosphors have potential applications in white light-emitting diodes.