Luminescence characterization of rare earth (RE = Tb, Dy, Eu) ions activated Ca8NaGd(PO4)6F2 halophosphor synthesis by modified Pechini method
Bharti Bawanthade,Ashok Mistry,Vidya Bawanthade,Ashish Mathur,Sanjay J. Dhoble
DOI: https://doi.org/10.1007/s10854-024-12525-4
2024-04-20
Journal of Materials Science Materials in Electronics
Abstract:Fluorapatite composites Ca 8 NaGd(PO 4 ) 6 F 2 :Dy 3+ , Tb 3+ , and Eu 3+ were successfully synthesised for the first time by the modified Pechini method for different concentrations of Dy, Tb, and Eu. As synthesised, Ca 8 NaGd(PO 4 ) 6 F 2 : x % Dy, Tb, and Eu show intense emission in the blue, green, and red regions, respectively. In Ca 8 NaGd(PO 4 ) 6 F 2 : x %Tb 3+ , Dy 3+ shows intense green and blue emission at λ ex = 274 nm, which confirms energy transfer from Gd 3+ to Tb 3+ and Gd 3+ to Dy 3+ . Under λ ex = 274 nm Ca 8 NaGd(PO 4 ) 6 F 2 : x %Eu 3+ , yellow emission is more intense, while at λ ex = 392 nm red emission is more dominant. Ca 8 NaGd(PO 4 ) 6 F 2 with 1% Tb 3+ has a longer decay time of 3.25 ms as compared with that of 1% Dy 3+ and 10% Eu 3+ , which have 1.73 ms and 2.27 ms, respectively. Ca 8 NaGd(PO 4 ) 6 F 2 doped with 5% Eu 3+ has a comparatively higher band gap (3.919 eV) than 1% Dy 3+ (3.918 eV) and Tb 3+ (3.914 eV) obtained from the Tauc plot. Ca 8 NaGd(PO 4 ) 6 F 2 without an activator shows self-emission at 316 nm under λ ex = 274 nm in the NBUVB region. On analysing the optical properties of the as-prepared Ca 8 NaGd(PO 4 ) 6 F 2, authors suggest that an undoped matrix can be used for phototherapy and that a matrix doped with Eu 3+ , Tb 3+ , and Dy 3+ activator ions becomes a useful candidate for the generation of white LEDs due to emission in the red, green, and blue regions, respectively, with good optical qualities.
engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied