Abstract:Improving the hot workability and reducing the processing cost are critical steps to expanding the application of TiC/Ti-6Al-4V composites. This study employed melt hydrogenation to fabricate TiC/Ti-6Al-4V composites under a mixed atmosphere of hydrogen and argon. Experimental results indicated that hydrogen had an obvious influence on the growth and morphology of eutectic TiC particles, and the size of eutectic TiC and primary β grains was significantly increased. As a result, large-sized eutectic TiC was distributed along the grain boundaries of primary β grains. Hot compression results showed that the peak flowing stress of composites was reduced by hydrogen, which resulted in an improvement of hot workability, especially in the (α + β) phase region, and the best results were obtained at 900 °C/0.01 s−1, at which the peak stress decreased from 241 ± 9 to 190 ± 8 MPa (a decrease of 21.2%). Inspection of the microstructure after hot compression showed that hydrogen improved the proportion of DRX grains from ~62.7% to ~83.2%, and hydrogen also decreased the density of dislocations, which were attributed to hydrogen accelerating atomic diffusion. Enhanced hot workability resulted from hydrogen atoms decreasing the atomic bonding force of the titanium matrix, hydrogen reducing the β/(α + β) transition temperature, the higher proportion of DRX, and the higher mobility of dislocations. It is expected that the findings of this study may support the development of a simple and efficient method to reduce the processing cost of TiC/Ti-6Al-4V composites.

Positive Effect of Hydrogen on Interface of in Situ Synthesized Ti-6Al-4V Matrix Composites

Hydrogen Induced Microstructure Evolution of Titanium Matrix Composites

Effects of Melt Hydrogenation on the Microstructure Evolution and Hot Deformation Behavior of TiBw/Ti-6Al-4V Composites

Hydrogen-induced modification of the interface between matrix and ceramic phase of (TiB + TiC)/Ti–6Al–4V

Effect of Melt Hydrogenation on Microstructure Evolution and Tensile Properties of (tib + TiC)/Ti-6Al-4V Composites

High Temperature Deformation Behavior of Melt Hydrogenated (tib + Tic)/Ti-6al-4v Composites

Hydrogen Induced Softening and Hardening for Hot Workability of (tib + TiC)/Ti-6Al-4V Composites

Improvement In Hot Workability Of Titanium Matrix Composite By Thermohydrogen Treatment

Microstructure Evolution and Enhanced Hot Workability of TiC/Ti-6Al-4V Composites Fabricated by Melt Hydrogenation

Hydrogen-induced microstructure optimization and mechanical properties enhancement of forged (TiB + TiC)/Ti6Al4V

Effect of Hydrogen on Microstructure and High Temperature Deformation of (tib + TiC)/Ti–6Al–4V Composite

Effect of hydrogen on deformation induced phase transformation and hot workability of Ti2AlN/Ti46Al4Nb1Mo composites

Insights into hydrogen-induced strengthening mechanism of TiC/Ti6Al4V via experiments and first-principles calculations

Towards Enhancing the Hot Deformability of Ti2AlN/Ti46Al4Nb1Mo Composites Via Melt Hydrogenation

Exploration and Development of (tib + TiC)/Ti6Al4V Through the Economically Viable Melt Hydrogenation Technique

Effect of hydrogen on hot deformation behavior and microstructure evolution of Ti65 alloy

Effect of hydrogen on superplastic deformation of (TiB + TiC)/Ti-6Al-4V composite

Effects of Hydrogen on the Interfacial Reaction Between Ti 6al 4V Alloy Melt and Al2O3 Ceramic Shell

Towards enhancing the hot deformability of Ti 2 AlN/Ti46Al4Nb1Mo composites via melt hydrogenation

Effect of Hydrogen on the Microstructural Evolution of a Γ-Tial Based Alloy

Hot Deformation Behavior and Dynamic Recrystallization of Melt Hydrogenated Ti-6Al-4V Alloy