Ruthenium Dioxide-Decorated Carbonized Tubular Polypyrrole As a Bifunctional Catalyst for Non-Aqueous Lithium-Oxygen Batteries

R. H. Zhang,T. S. Zhao,P. Tan,M. C. Wu,H. R. Jiang

DOI: https://doi.org/10.1016/j.electacta.2017.10.097

IF: 6.6

2017-01-01

Electrochimica Acta

Abstract:Owing to large specific surface area, high electronical conductivity and low mass, carbon materials have been widely used as cathode for non-aqueous lithium-oxygen (Li-O2) batteries. However, carbon cathodes usually present poor catalytic activities toward oxygen reduction and evolution reactions (ORR and OER), resulting in a large charge over-potential and a short cycling life. In this work, a non-aqueous Li-O2 battery with a bifunctional catalyst, ruthenium dioxide (RuO2)-decorated carbonized tubular polypyrrole, is reported. Compared with conventional catalysts, the bifunctional catalyst has two special features: i), a high content of graphitic N, and ii), a large number of RuO2 nanoparticles. The battery with the novel bifunctional catalyst shows a large discharge capacity (10095mAhg−1 at a current density of 200mAg−1), a high rate capacity (6758mAhg−1 at a current density of 1000mAg−1) and a long cycling life (55 cycles at the current density of 500mAg−1). In addition, at the first cycle with a fixed capacity of 1000mAhg−1, the discharge and charge over-potentials are only 0.28 and 0.78V, which are 180 and 360mV lower than those of the batteries fitted with pristine carbonized tubular polypyrrole cathode.