Enhanced energy storage performance in SBNN-based tungsten bronze ceramics through co-substitution strategy in A/B sites

Suwan Li,Yan Wang,Lu Guo,Xiaolian Chao,Di Wu,Pengfei Liang,Zupei Yang,Jiangbo Lu,Lingling Wei

DOI: https://doi.org/10.1016/j.jallcom.2023.171044

IF: 6.2

2023-07-07

Journal of Alloys and Compounds

Abstract:Tungsten bronze lead-free (Sr 0.7 Ba 0.3 ) 2− x Bi x NaNb 5− x Ti x O 15 ceramics were fabricated via the traditional solid-state reaction method. The effects of co-doping Bi 3+ /Ti 4+ in A/B sites on the structures, relaxor characteristics, and energy storage performance were studied. All ceramics exhibited a pure TTB structure. The phase structure for all ceramics evolved from P 4 bm to P 4/ mbm symmetry with increasing content of the co-doping ions. The introduction of Bi 3+ and Ti 4+ , which have different valence states, may have caused random occupation of ions in both A and B sites and increased the distorting degree of BO 6 octahedra, leading to the merger of two dielectric anomalous peaks and dielectric relaxation. Finally, a relatively good energy storage density (1.8 J/cm 3 ) and an ultrahigh efficiency (87 %) were achieved under an applied electric field of 210 kV/cm for ceramics with x = 0.20. Moreover, the energy storage densities and efficiencies were stable over a large number of cycles (10 5 times). This demonstrates the potential of these ceramics for application as dielectric capacitors.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering