Abstract:In this paper, the loading rate–dependent tensile damage and fracture behavior of fiber-reinforced ceramic-matrix composites (CMCs) are investigated. A micromechanical tensile constitutive model is developed considering multiple tensile damage mechanisms. A new parameter of the interface debonding rate is proposed to characterize the strain rate–dependent tensile damage evolution in fiber-reinforced CMCs. Experimental tensile stress-strain curves, composite's tangent modulus, interface debonding ratio, and probability of fiber's breakage in unidirectional SiC/CAS-II, 2D plain-woven CVI C/SiC and SiC/SiC, 2.5D woven CVI C/SiC, and 3D woven CVI and PIP SiC/SiC composites are predicted for different strain rates at room and elevated temperatures. Effects of fiber's preforms, testing temperature, and fabrication method on the loading rate–dependent tensile damage and fracture behavior of fiber-reinforced CMCs are analyzed. Relationships between composite's microstructure, mechanical behavior, and strain rate for different CMCs are established. The rate of interface debonding increased with increasing strain rate and was the highest for unidirectional SiC/CAS-II, and the lowest for 3D woven SiC/SiC, and the rate of interface debonding was independent of testing temperature. For unidirectional SiC/CAS-II and 2D plain-woven CVI SiC/SiC composites, when the loading rate increased, the proportional limit stress, tensile strength, and fracture strain increased; and, for 2.5D woven CVI C/SiC and 3D woven CVI SiC/SiC, when the loading rate increased, the proportional limit stress, composite tensile strength, and fracture strain decreased.

Effects of Micro-Damage on the Nonlinear Constitutive Behavior of SiC / SiC Minicomposites

Application and Analysis of Plane Woven C/Sic Composites Based on Continuum Damage Mechanics

Damage Theoretical Analysis of 2.5D C/SiC Composites under Tensile and Shear Loading

Damage Evolution and Fracture Behavior of C/SiC Minicomposites with Different Interphases under Uniaxial Tensile Load

Effect of Stochastic Loading on Tensile Damage and Fracture of Fiber-Reinforced Ceramic-Matrix Composites

Damage failure mechanism of unidirectional fiber reinforced SiC f /SiC composites under uniaxial tension

Damage Failure Mechanism of Unidirectional Fiber Reinforced SiCf/SiC Composites under Uniaxial Tension

A Damage Constitutive Model for the Nonlinear Mechanical Behavior of C/SiC Composites During Mechanical Cyclical Loading/unloading

Modeling Tensile Damage and Fracture Behavior of Fiber-Reinforced Ceramic-Matrix Minicomposites

Modeling of Nonlinear Mechanical Behavior for 3d Needled C/C-Sic Composites under Tensile Load

DAMAGE EVOLUTION AND MICROSTRUCTURAL CHARACTERIZATION OF A CROSS-WOVEN C/SiC COMPOSITE UNDER TENSILE LOADING

In-situ Tensile Damage and Fracture Behavior of PIP SiC/SiC Minicomposites at Room Temperature

Damage Characteristics and Constitutive Modeling of the 2D C/SiC Composite: Part II – Material Model and Numerical Implementation

Damage Characteristics and Constitutive Modeling of the 2D C/SiC Composite: Part I – Experiment and Analysis

In Situ Damage Propagation and Fracture in Notched Cross-Ply SiC/SiC Composites: Experiment and Numerical Modeling

Shear nonlinear constitutive relationship of needled C/C-SiC composite

Micromechanical modeling of loading rate–dependent tensile damage and fracture behavior in fiber-reinforced ceramic-matrix composites

Characterisation of damage evolution in plain weave SiC/SiC composites using in situ X-ray micro-computed tomography

Tensile Behaviour and Damage Evolution of A C/Sic Minicomposite Fabricated by Chemical Vapour Infiltration

Damage Behavior of 2.5-C/SiC Composite under Tensile Loading: Damage Behavior of 2.5-C/SiC Composite under Tensile Loading

Micromechanical Modeling Tensile and Fatigue Behavior of Fiber-Reinforced Ceramic-Matrix Composites Considering Matrix Fragmentation and Closure