Abstract:In the present work, phase equilibria in the Li O–Al O system were experimentally studied and calorimetric measurements were performed. Based on obtained results and data from literature, thermodynamic parameters of the system were assessed. The solid solution phases were modeled using Compound Energy Formalism (CEF) and liquid phase was described by two-sublattice partially ionic liquid model. The experimental investigations for selected compositions of isothermally heat-treated samples were performed using x-ray Diffraction (XRD) and Scanning Electron Microscopy (SEM). Differential Thermal Analysis (DTA) and Differential Scanning Calorimetry (DSC) were used to measure the temperature of the reactions as well as the heat capacities, respectively. After DTA, the microstructure was analyzed using SEM. Temperature of peritectic melting of h-LiAl O was determined to be 2222 K and temperature of eutectic reaction Liq -LiAlO + h-LiAl O to be 1965 K. Heat capacity of LiAlO and LiAl O was measured in the temperature range of 100-1300 K. The degree of inversion of spinel phase (Al , Li ) :(Al , Li , Va) :O was modelled assuming Al and Li can occupy tetrahedral (T) and octahedral (O) cationic sublattices while its composition extension in Al O enriched region was described by introducing vacancies in octahedral sites. Thermodynamic description derived in the present study reproduces the degree of inversion close to that of the high-temperature spinel phase, which means that Al ions preferentially occupy the tetrahedral sites. The calculated phase diagram satisfactorily agrees with the experimental results. Available experimental thermodynamic data are also reproduced within uncertainty limits.

Experimental Determination and Thermodynamic Calculation of BaO-In2O3-B2O3 System

Measurement And Modeling Of The High-Pressure Phase Behavior Of The Carbon Dioxide Plus Propene Oxide Binary System

Thermodynamic investigation on the Al2O3–BaO binary system

Assessment of the thermodynamics and phase diagram of the SrO-B2O3 system

Thermodynamic Optimization of BaO-MgO Binary System

Structure and Thermodynamic Properties of Beo: Empirical Corrections in the Quasiharmonic Approximation

Experimental Investigation and Thermodynamic Modeling of the Li O–Al O System

Phase equilibria in the TiO2–Nb2O5 system: New experiments and thermodynamic modeling

Phase equilibrium investigations of the Al2O3–Ta2O5 system: New experiments and thermodynamic modeling

Thermodynamic Basis and Related Phase Equilibria for In-Na and In-Ca Binary Systems

Phase relations of BaCoO3−δ–BaInO2.5 and size variation effect of B-site cations on the phase transitions

First-principles Investigation of the Structural, Mechanical and Thermodynamic Properties of Al2Cu Phase under Various Pressure and Temperature Conditions

Phase equilibria studies in the CaO–SiO 2 –Al 2 O 3 –MgO system with CaO/SiO 2 ratio of 0.9

Phase equilibria and thermodynamic assessment of the Al2O3-SiO2-Sc2O3 system

Phase equilibria in the La2O3-Sm2O3-ZrO2 system: Experimental studies and thermodynamic modeling

Thermodynamic Assessment of the P2O5-Na2O and P2O5-MgO Systems

Phase Equilibrium of the In<sub>2</sub>O<sub>3</sub>−TiO<sub>2</sub>−MO (M = Ca, Sr) Systems and the Structure of In<sub>6</sub>Ti<sub>6</sub>CaO<sub>22</sub>

Thermodynamic evaluation and optimization of the K2O‐Al2O3‐SiO2 system

Internally Consistent Thermodynamic Data and Equilibrium Phase Relations for Compounds in the System MgO‐SiO2 at High Pressure and High Temperature

Phase equilibria in the ZrO 2 –Ta 2 O 5 –Nb 2 O 5 system: Experimental studies and thermodynamic modeling

Phase Equilibrium Investigations and Thermodynamic Study of the Y2O3-Ta2O5 System