Abstract:In this report, a series of N-doped porous carbon materials were successfully prepared from nitrogen-containing porous organic framework JUC-Z2. Compared to original JUC-Z2, the carbonized samples show obviously enhanced gas uptake and isosteric heats of adsorption ( Q st for short). Among the carbonized samples, JUC-Z2-900 shows high CO 2 uptake of 113 cm 3 •g － 1 at 273 K and 1 bar and H 2 sorption of 246 cm 3 •g － 1 at 77 K and 1 bar, surpassing most reported porous materials. Especially for CH 4 sorption, a large sorption amount of 60 cm 3 •g － 1 could be achieved at 273 K and 1 bar. To our best knowledge, this value is comparable to the highest among all the porous materials reported to date. Apart from high gas uptake, the carbon materials also show selective adsorption ability. At 273 K, JUC-Z2-900 shows a high CO 2 /N 2 adsorption selectivity of 10 and CO 2 /H 2 adsorption selectivity of 66. Raman spectra showed two Raman shifts, the G-band at 1590 cm － 1 is associated with the E 2g mode of graphite, whereas the D-band centered at around 1360 cm － 1 is attributed to the D-band of disordered carbon, corresponding to the defect-induced mode. The intensity of D-band is higher than G-band, indicating a low degree of graphitization. This is also confirmed by powder X-ray diffraction results. X-ray Photoelectron Spectroscopy (XPS) results indicate the nitrogen content is 3.26 wt%, 2.88 wt% and 2.19 wt% for JUC-Z2-700, JUC-Z2-800 and JUC-Z2-900 respectively. Though the nitrogen content decreased after carbonization, the gas sorption increased greatly. This can be attributed to the increased heat of adsorption of the carbonized samples. First, the narrow pore size after carbonization is beneficial for gas storage. Reports indicate that by tuning the pore sizes to around the kinetic diameter of CO 2 , it may be possible to increase the number of double or multiple interactions between the adsorbed CO 2 and the pore walls. Second, the all-carbon-scaffold networks also benefit the gas-adsorbent interaction. Last but not the least, the N-doped framework also devote the high gas uptake. Besides the high gas uptake, the carbon materials exhibit high thermal stabilities and could be stable up to 500 ℃ . Based on the above results, the carbon materials show great potential in the fields of CO 2 capture and clean energy storage.

Zif-Derived In Situ Nitrogen Decorated Porous Carbons For Co2 Capture

Enhanced CO2 Adsorption Performance on Hierarchical Porous ZSM-5 Zeolite

Efficient CO2 Capture by ZIF-8-derived In-Situ Nitrogen-Doped Nanoporous Carbon with Ultra-High Selectivity and Stability

Structurally Designed Synthesis of Mechanically Stable Poly(benzoxazine-co-resol)-Based Porous Carbon Monoliths and Their Application As High-Performance CO2 Capture Sorbents

Facile Synthesis of MOF-5-derived Porous Carbon with Adjustable Pore Size for CO2 Capture

Preparation of N-doped Porous Carbon from Porous Organic Framework for Gas Sorption

Highly Nitrogen-Doped Porous Carbon Derived from Zeolitic Imidazolate Framework-8 for CO2 Capture

Nitrogen-Doped Ultrahigh Microporous Carbons Derived from Two Nitrogen-Containing Post-Cross-Linked Polymers for Efficient CO2 Capture

Enhancing CO 2 adsorption performance of porous nitrogen-doped carbon materials derived from ZIFs: Insights into pore structure and surface chemistry

In-situ Co-Growth of ZIF-8-derived Bio-Carbon Spheres with Meso-Macroporous Hierarchy for Stable and Rapid Carbon Dioxide Capture

Tailored Pore Structure of ZIF-8/chitosan-derived Carbonaceous Adsorbent by Introducing Mesoporous Silica Nanoparticles for Superior CO 2 Uptake

Benzimidazole Precursor-Derived N-Doping Porous Carbon with High-Efficiency Co2 Selective Adsorption: Insight from Experimental and Theoretical Study

Preparation of Zeolitic Imidazolate Framework-8-Based Nanofiber Composites for Carbon Dioxide Adsorption

Chitosan Derived Nitrogen-Doped Microporous Carbons for High Performance CO2 Capture

A Novel ZIF-8@cellulose Composite Monolithic Carbon Via a Facile Template-Free Strategy for Selective and Efficient CO2 Adsorption

Bifunctional Hno3 Catalytic Synthesis Of N-Doped Porous Carbons For Co2 Capture

PEG-templated synthesis of ultramicroporous n-ZIF-67 nanoparticles with high selectivity for the adsorption and uptake of CO2 over CH4 and N2

Fabricating Self-Templated and N-doped Hierarchical Porous Carbon Spheres Via Microfluidic Strategy for Enhanced CO2 Capture

N/S co-doped microporous zeolite-templated carbon for efficient CO 2 adsorption and separation

Green and Rapid Synthesis of Hierarchical Porous Zeolitic Imidazolate Frameworks for Enhanced CO2 Capture

Construction of Ultramicropore-Enriched N-doped Carbons for CO2 Capture: Self-decomposition of Polyethyleneimine-Based Precursor to Promote Pore Formation and Surface Polarity