Nitrogen-rich hollow carbon microspheres with tunable shell thicknesses for enhanced CO2 adsorption
Qun-Yan Li,Xuan Gao,Shou-De Han,Jun-Guo Liu,Ya-Li Wang,Qi Wei,Su-Ping Cui,Zuo-Ren Nie
DOI: https://doi.org/10.1007/s10971-024-06338-4
2024-02-21
Journal of Sol-Gel Science and Technology
Abstract:Nitrogen-rich hollow carbon microspheres were successfully synthesized using resorcinol and formaldehyde as carbon sources, tetraethylenepentamine (TEPA) as a catalyst, and nitrogen source, with SiO2 microspheres as a hollow template. The hollow carbon microspheres were prepared by adding varying amounts of SiO 2 hollow templates to a fixed amount of TEPA. The shell thickness increased as the amount of SiO 2 template decreased and the shell thicknesses of AHMCS-2(1), AHMCS-2(3), and AHMCS-2(5) were 28.5 nm, 17.3 nm, and 12.7 nm, respectively. The activated hollow carbon microspheres (AHMCS-2(1), AHMCS-2(3) and AHMCS-2(5)) contained 4.66%, 5.05%, and 3.27% nitrogen, respectively. Due to the sufficient activation process, the specific surface area and microporous volume of hollow carbon microspheres are greatly increased compared to solid carbon microspheres, therefore, their CO 2 adsorption performance is superior as well. As the shell layer thickens, the specific surface area and micropore volume of the activated hollow carbon microspheres increased, among which AHMCS-2(1) showed the largest specific surface area and micropore volume of 1146 m 2 /g and 0.45 cm 3 /g, respectively. Similarly, the CO 2 adsorption capacity of activated hollow carbon microspheres increased with the increasing thickness of the shell layer, and that of AHMCS-2(1) reached 5.54 mmol/g at 0 °C. High specific surface area, high micropore volume, high nitrogen content, and small micropore pore size are favorable for CO 2 adsorption by carbon microspheres. The hollow carbon microspheres exhibit high CO 2 dynamic adsorption capacity, excellent selective adsorption, and good cyclic stability.
materials science, ceramics