Thixoforming-forging compound forming technology for 6A02 Al bracket-shape component
Ying Zhang,Jufu Jiang,Ying Wang,Yingze Liu,Minjie Huang
DOI: https://doi.org/10.1016/j.ijmecsci.2022.107881
IF: 7.3
2022-10-28
International Journal of Mechanical Sciences
Abstract:Conventional thixoforming technology had advantages of casting and forging, but low plastic deformation degree and existence of liquid phase lowered the mechanical property. In this work, 6A02 bracket-shape component was firstly manufactured by the efficient thixoforming-forging compound forming technology and bimodal semisolid billet. Bimodal semisolid feedstock was beneficial for both filling ability and mechanical strength due to intragranular dislocation and elongated grain shape. Firstly, a Deform-3D simulation of compound forming was established by controlling temperature field distribution. Then the effects of billet shapes, billet temperatures, soaking times, mold temperatures and dwell times on microstructures and mechanical properties were investigated. Though the mechanical strength and ductility at the shoulder were elevated by larger plastic deformation in the integrated forming process, they were still lower than those at side wall and bottom part in virtue of liquid segregation. Besides, the largest yield strength σ y , tensile strength σ max and elongation δ of compound-formed 6A02 components were even 16.8%, 25.8%, and 77.6% higher than σ y , σ max and δ of 6A02 hot-extruded bar, respectively. Finally, the deformation behavior and strengthening mechanism of compound forming technology were discussed deeply. Particularly, except liquid fraction, deformation behavior was relevant with grain size and morphology. For rounder and smaller grains, grain boundary sliding was dominant. But slip deformation was predominant for large-deformed grains. Subsequently, a new dynamic recrystallization (DRX) mechanism was proposed and only continuous dynamic recrystallization (CDRX) could make the wet grain boundary serrated. A quantitative insight into strengthening mechanism indicated that solid solution strengthening and dislocation strengthening were dominant. This study provided a theoretical guidance and experimental support for the efficient application and forming control of 6A02 alloy in compound forming area.
engineering, mechanical,mechanics