Abstract:Novel anion exchange membranes (AEMs), based on poly(phenylene oxide) (PPO) chains linked to pendant 1,2-dimethylimidazolium (DIm) functional groups, have been prepared for evaluation in alkaline polymer electrolyte membrane fuel cells (APEFCs). Successful functionalisation of the PPO chains was confirmed using H-1-NMR and FT-IR spectroscopies. The ionic conductivities of the resulting DIm-PPO AEMs at 30 degrees C are in the ranges of 10-40 mS cm(-1) and 18-75 mS cm(-1) at 60 degrees C. The high ionic conductivities are attributed to the highly developed microstructures of the membranes, which feature well-defined and interconnected ionic channels (confirmed by atomic force microscopy, AFM, measurements). Promisingly, the ion-exchange capacities (IECs) of the DIm-PPO AEM are maintained after immersion in an aqueous KOH solution (2 mol dm(-3)) for 219 h at 25 degrees C; a previously developed monomethyl imidazolium PPO analogue AEM (Im-PPO) showed a significant decline in IEC on similar treatment. This reduction in undesirable attack by the OH- conducting anions is ascribed to an increase in steric interference and removal of the acidic C2 proton [in the monomethyl Im-groups] by the methyl group in the DIm cationic ring. Moreover, the maximum power densities produced in simple beginning-of-life single cell H-2/O-2 fuel cell tests increased from 30 mW cm (2) to 56 mW cm (2) when switching from the Im-PPO AEM (fuel cell temperature = 50 degrees C) to the DIm-PPO-0.54 AEM (fuel cell temperature = 35 degrees C) respectively (even with the use of lower temperatures).

Long-spacer-chain imidazolium functionalized poly(ether ether ketone) as hydroxide exchange membrane for fuel cell

Poly (ether ether ketone ketone) based imidazolium as anion exchange membranes for alkaline fuel cells

Quaternized Poly(phthalazinone Ether Ketone) Membranes for Alkaline Fuel Cells

Imidazolium-Functionalized Poly(Ether Ether Ketone) As Membrane and Electrode Ionomer for Low-Temperature Alkaline Membrane Direct Methanol Fuel Cell

Branched Poly(ether Ether Ketone) Based Anion Exchange Membrane for H2/O2 Fuel Cell

Anion exchange membranes with fast ion transport channels driven by cation-dipole interactions for alkaline fuel cells

Quaternized Poly(ether Ether Ketone) Hydroxide Exchange Membranes for Fuel Cells

Cross-linked Hydroxide Conductive Membranes with Side Chains for Direct Methanol Fuel Cell Applications

Development of imidazolium-type alkaline anion exchange membranes for fuel cell application

High-strength anion-exchange fuel cell membranes based on imidazole-functionalized poly-ether-ether-ketone materials

Hydrophilic–Hydrophobic Bulky Units Modified Anion Exchange Membranes for Fuel Cell Application

Synthesis and Properties of a Novel Side-Chain-type Hydroxide Exchange Membrane for Direct Methanol Fuel Cells (Dmfcs)

Anion Exchange Membranes Based on Sulfonated Poly(ether ether ketone) Crosslinked Methylpyrrolidinium Functionalized Poly (vinyl benzyl chloride) with High Chemical Stability

Alkaline polymer electrolytes containing pendant dimethylimidazolium groups for alkaline membrane fuel cells

Porous PTFE supported bis(siloxane imidazole) functionalized Norbornyl copolymer composite anion exchange membrane for alkaline fuel cells

Anion Exchange Membranes with "Rigid-Side-chain" Symmetric Piperazinium Structures for Fuel Cell Exceeding 1.2 W Cm−2 at 60 °C

Hydroxide exchange composite membrane based on soluble quaternized polyetherimide for potential applications in fuel cells

Poly(2,6-dimethyl-1,4-phenylene oxide) containing imidazolium-terminated long side chains as hydroxide exchange membranes with improved conductivity

Intrinsic microporous poly(phenyl-alkane)s with pendent piperazinium for high performance anion exchange membrane fuel cells

High durable poly(vinyl alcohol)/Quaterized hydroxyethylcellulose ethoxylate anion exchange membranes for direct methanol alkaline fuel cells

Cationic metal–organic framework porous membranes with high hydroxide conductivity and alkaline resistance for fuel cells