Rb3MgB5O10 and LiBaAl(BO3)2: Covalent Tetrahedra MO4-Containing Borates with Deep-ultraviolet Cutoff Edges
Hongkang Su,Jiahao Jiao,Shibin Wang,Donghai An,Min Zhang
DOI: https://doi.org/10.1039/d3dt03288d
IF: 4
2023-12-08
Dalton Transactions
Abstract:Borates are favored by material scientists and chemists because of the significant electronegativity difference between B and O atoms and their flexible assembly modes resulting in abundant structures and excellent properties. For the design of deep-ultraviolet (DUV) optical crystals with excellent macroscopic performance, it is crucial to choose appropriate cations and anionic groups, and microscopically reasonable assembly patterns. Herein, by introducing covalent tetrahedra ([MO4], M = Mg, Al), two new mixed alkali metals and alkaline earth metals borates, Rb3MgB5O10 and LiBaAl(BO3)2, were synthesized using the melt method and high-temperature solution method. They contain M-B-O two-dimensional (2D) layers (2∞[MgB5O10] and 2∞[Al(BO3)2], respectively) composed of isolated B-O groups ([B5O10]5- and [BO3]3-, respectively) and metal-centered tetrahedral connectors ([MgO4]6- and [AlO4]5-, respectively). Combining experiments and theoretical calculations shows that the two compounds have short cutoff edges (<200 nm) and moderate birefringences. Further analysis manifests that the isolated [MO4] covalent tetrahedra can optimize the arrangement of anion groups, guarantee the balanced optical properties of materials, and points out the direction for further exploration of novel borate structures.
chemistry, inorganic & nuclear