Gradient Nanotwinned Structure and Its Formation Mechanism in Inconel 625 Alloy Produced by Surface Mechanical Grinding Treatment
Yuanjun Ma,Yutian Ding,Yubi Gao,Jianjun Chen,Xingmao Wang
DOI: https://doi.org/10.1007/s12540-022-01297-3
IF: 3.451
2022-09-12
Metals and Materials International
Abstract:Effects of surface mechanical grinding treatment on the structure evolution and grain refinements of gradient structured surface layer on Inconel 625 have been studied. The results showed that a 600 μm thick gradient nanotwinned (GNT) structure layer could be successfully constructed in the superficial layer of the alloy by adjusting the process parameters. The TEM characterization revealed that a gradient change from nano-grain and nanotwinned to dislocation structure was formed in the alloy structure, and the grain size of the outermost layer of the alloy could be refined to 18 nm, with a thickness of up to 30 μm and a surface hardness of 7.4 GPa. In addition, with an increase in the layer depth, twinning played a major role in the refinement. Firstly, a high-density twin/matrix lamellar structure was formed in the microstructure at high strain rates during the process of plastic-induced grain refinement, and the original coarse grains were refined. During further deformation, due to the increasing difficulty of work hardening and the reactions between dislocations and twin boundaries, the lamellar structure was sheared and broken into equiaxed nanocrystals. Finally, the nanocrystals were further refined to a smaller size through twinning. During this process, twinning is more likely to occur for a grain size of 71–80 nm. These findings shed light on the basic principle of GNT construction, especially the twinning induced grain refinement mechanism under different grain sizes. Graphical
materials science, multidisciplinary,metallurgy & metallurgical engineering