Structural behavior and in vitro bioactivity evaluation of hydroxyapatite-like bioactive glass based on the SiO2-CaO-P2O5 system
Cuilian Wen,Nuonan Bai,Lijin Luo,Jianxia Ye,Xuan Zhan,Yinggan Zhang,Baisheng Sa
DOI: https://doi.org/10.1016/j.ceramint.2021.03.125
IF: 5.532
2021-07-01
Ceramics International
Abstract:Silicate bioglass is of great importance in bone engineering because of its excellent bioactivity and osteogenic effects. In this study, hydroxyapatite-like bioactive glass based on the xSiO2-CaO-P2O5 (x = 30, 45, 60 and 90 mol.%, Ca/P = 1.67) system was synthesized by the sol-gel method, and the corresponding structural evolution, apatite-forming ability and cytotoxicity were systematically investigated. The results suggest that both a higher heat treatment temperature and a lower SiO2 content increase the crystallinity tendency of the bioglass, and the samples become obviously compact as the SiO2 amount increases from 30 to 90 mol.%. Compared with the samples with higher SiO2 content, the 30Si sample shows more remarkable internal connected mesoporous structures, with a higher specific surface area up to 129.12 m2/g, exhibiting excellent hydroxyapatite formation in simulated body fluid. Moreover, no obvious inhibitory effect was presented on human periodontal ligament cells (hPDLCs) for any of the silicate glass samples.
materials science, ceramics