Abstract:Utilizing MgO as the precursor and deionized water as the solvent, this study synthesized nanoparticles of Mg(OH)2 via hydrothermal methods, aiming to control its purity, particle size, and morphology by understanding its growth under non-uniform nucleation. Characterization of crystal morphology and structure was conducted through scanning electron microscopy and X-ray diffraction, while laser particle size detection assessed the secondary particle size distribution. The study focused on how MgO's hydrothermal process conditions influence Mg(OH)2 crystal growth, particularly through ion concentration and release rate adjustments to direct crystal growth facets. These adjustments shifted the dominant growth plane, enhancing the peak intensity ratio I001/I101 from 1.03 to 2.14, thereby reducing surface polarity and secondary aggregation of crystals. The study of the physicochemical properties of the same sample at different times revealed the pattern of crystal dissolution and recrystallization. A 2 h hydrothermal reaction notably altered the particle size distribution, with a decrease in particles sized 0.2~0.4 μm and an increase in those sized 0.4~0.6 μm, alongside new particles over 1 μm, indicating a shift toward uniformity through dissolution and recrystallization. Optimal conditions (6% magnesium oxide concentration, 160 °C, 2 h) led to the synthesis of highly dispersed, uniformly sized magnesium hydroxide, showcasing a simple, eco-friendly, and high-yield process.

Synthesis of Superfine Mg(OH)_2 Particles by Hydration of MgO in Alkali Solutions

Synthesis of superfine Mg(OH)2 particles by magnesite

Additives Applied for Preparation of Superfine Mg(Oh)(2) Particles by Light-Burned Mgo at Low Temperature

Synthesis of Mg(Oh)(2) Nanoparticles from Mgo Using Magnesium Acetate As Additive

Magnesium Nitrate As Additive for Synthesis of Mg(OH)2 Nanoparticles

Investigation of Crystallization Growth Characteristics of Mg(OH)2 Crystals under Unconstrained Conditions

The Influence of Processing Conditions for the Preparation of Super-fine Hydroxide Magnesium by Hydrating Method

Synthesis and characterization of MgSO4·5Mg(OH)2·2H2O flake powders

Nanoscale magnesium hydroxide and magnesium oxide powders: Control over size, shape, and structure via hydrothermal synthesis

Influence of synthesis condition on magnesium hydroxide properties by two-step reaction on pilot scale

Emulsion-phase Synthesis of Honeycomb-Like Mg5(OH)2(CO3)4·4H2O Micro-Spheres and Subsequent Decomposition to MgO

Preparation of highly-dispersed Mg(OH)2 powders and influence factors

Microwave-assisted synthesis of fibre-like Mg(OH)2 nanoparticles in aqueous solution at room temperature

Preparation and Characterization of Magnesium Hydroxide Sulfate Hydrate Whiskers

Hydrothermal Formation of Dispersive Mg(Oh)(2) Particles in Naoh Solution

Preparation and characterization of lamellar-like Mg(OH)2 nanostructures via natural oxidation of Mg metal in formamide/water mixture

Formation of rod-like Mg(OH)2 nanocrystallites under hydrothermal conditions and the conversion to MgO nanorods by thermal dehydration

Hydrolysis Process and Mechanism of Magnesium Aluminate Alkoxides

Hydrothermal formation and characterization of magnesium oxysulfate whiskers

Hydrothermal Synthesis Process of Magnesium Oxysulfate Whiskers

Hydrothermal Modification of Mg(OH)2 Particles in NaOH Solution