Effect of Vanadium on Properties of 18Cr-2Mo Ferritic Stainless Steel

李达岗,江来珠,金学军,王治宇,许海刚

DOI: https://doi.org/10.13228/j.boyuan.issn1001-0963.2013.02.002

2013-01-01

Abstract:Thermo-Calc software, scanning electron microscope (SEM), X-ray diffraction (XRD) and transmission electron microscope (TEM) were used to investigate the effect of vanadium (V) on the microstructure, mechanical properties and pitting corrosion resistance of 18Cr-2Mo ferritic stainless steel stabilized by niobium (Nb). The results show that the precipitates are mainly composed of NbC and VN which are dispersed in the intragranular and grain boundary, and the size of most of NbC particles is in the range from 100 to 250nm. The grain size and yield strength of materials nearly keep the same with different V addition amount under the condition of ultra-low C and N content, while the impact toughness and pitting resistance are improved gradually with the increasing of V. With the addition of 0. 36% V (mass fraction), the ductile to brittle transition temperature (DBTT) of the steel is decreased from -10 to -30 °C, and the pitting potential (Ep) is improved from 0. 38 to 0. 42 V.