Factors Influencing Cathodic Electrodeposition Coating Process

梁栋,任碧野,王朝阳,童真

DOI: https://doi.org/10.3969/j.issn.0253-4312.2002.09.009

2002-01-01

Abstract:This paper has described the factors that influence the film performance during cathodic electrodeposition process,and proposed some practical measures for solution.

What problem does this paper attempt to address?

Effect of Process Parameters on Electrodeposition Process of Co-Mo Alloy Coatings

Xiang Nan,Fu Wang,Sensen Xin,Xuewei Zhu,Qiongyu Zhou

DOI: https://doi.org/10.3390/coatings13040665

IF: 3.236

2023-03-24

Coatings

Abstract:Plating bath composition, temperature, current density, and pH have a great influence on the properties of a Co-Mo alloy coating. However, these conclusions are obtained from the perspective of test results. Most of the factors that affect the properties of the coating operate by interfering with the electrodeposition process. Therefore, it is of great significance to study the kinetics of the electrodeposition process. To further study the influence of process parameters on the deposition process of Co-Mo alloy coatings, cyclic voltammetry (CV), scanning linear voltammetry (LSV), and electrochemical impedance testing (EIS) were used to study the deposition kinetics of Co-Mo alloy coatings. The results show that with the increase in sodium molybdate content in the plating solution, more Mo elements are involved in the deposition process. At the same time, a higher Mo element content can reduce the dissolution of the coating as the anode and improve the service life of the coating, but too high a Mo element content will lead to cracks on the surface of the coating. The deposition temperature will affect the processes of reduction deposition and oxidation dissolution of the coating. The pH of the plating bath will directly affect the reduction reaction process of MoO42− ions in the plating bath. With the increase in the pH value, the reduction reaction rate of MoO42− ions decreases, and the cathodic reduction reaction current density decreases. At the same time, the peak current density of anodizing decreases with the decrease in the pH value of the plating solution, indicating that the alkaline plating solution has an inhibitory effect on the plating dissolution process.

materials science, multidisciplinary,physics, applied, coatings & films
The Study of Thin Film High–voltage Li-Ion Cathodes to Reveal Surface Reactions and Coating Performance

Juchuan Li,Yoongu Kim,Chengdu Liang,Nancy J Dudney

DOI: https://doi.org/10.1149/ma2013-02/13/930

2013-01-01

ECS Meeting Abstracts

Abstract:The performance of high-voltage lithium intercalati on cathodes are limited because of reactions with the standard LiPF6 carbonate electrolytes and possibly changes in the crystalline lattice when charged to voltages above about 4.3V versus lithium. By using thin film s of the cathode materials, prepared by sputter depositi on processing, it becomes feasible to identify and stu dy reaction and degradation processes that are specifi c to the cathode compound. Further, the performance of vari ous protective coatings can be investigated with good c ntrol and variation of the coating thickness and coverage at the interface.
Influence of Electrodeposition Conditions on the Microstructure and Corrosion Resistance of Zn–Ni Alloy Coatings from a Deep Eutectic Solvent

S. Fashu,C. D. Gu,X. L. Wang,J. P. Tu

DOI: https://doi.org/10.1016/j.surfcoat.2014.01.014

2014-01-01

Abstract:The collective influence of crucial electrodeposition parameters (temperature, deposition voltage and bath composition) on the properties of Zn–Ni films electrodeposited in a choline chloride–urea eutectic-based ionic liquid was investigated. The microstructures, chemical compositions, phase structures and corrosion behaviors of electrodeposited films were analyzed using scanning electron microscope, energy dispersive X-ray spectroscopy, X-ray diffraction and linear cyclic voltammetry, respectively. The surface morphologies and chemical compositions of the films were strongly dependent on the electrodeposition parameters. It was found that the amounts of nickel in the Zn–Ni alloy films were significantly higher than that present in the electrolytes and was always above 50%, indicating normal codeposition mechanism. Electrodeposition of high Zn content alloy is favorable at high electrodeposition voltages, high temperatures and high Zn (II)/Ni (II) ratios. Electrochemical measurements shows that under the conditions considered, the Zn–Ni film from 0.45M Zn (II)–0.05M Ni (II) deposited at 55°C and 0.8V exhibits the highest barrier corrosion resistance compared with the other films and this was attributed to a dense, smooth and crack free morphology with optimum Zn content.
Electrochemical Performance of Electroactive Poly(Amic Acid)-Cu2+ Composites

Ying Yan,Fangfei Li,Ashley M. Hanlon,Erik B. Berda,Xincai Liu,Ce Wang,Danming Chao

DOI: https://doi.org/10.1016/j.apsusc.2016.09.012

IF: 6.7

2017-01-01

Applied Surface Science

Abstract:Electroactive poly(amic acid)-Cu2+ (EPAA-Cu) composites on substrates were successfully prepared via nucleophilic polycondensation followed by the use of an immersing method. Analysis of the structure properties of EPAA-Cu composites was performed using scanning electron microscopy (SEM), X-ray photoelectron spectra (XPS) and Fourier-transform infrared spectra (FTIR). A significant current enhancement phenomenon of EPAA-Cu/ITO electrodes was found as evident from cyclic voltammetry (CV) measurements. In addition, Cu2+ ions were incorporated into the composites and had a positive effect on their electrochromic behaviors decreasing their switching times. The anticorrosive performance of EPAA-Cu composites coatings on the carbon steel in 3.5 wt%NaCl solution were also investigated in detail using tafel plots analysis and electrochemical impedance spectroscopy. The anticorrosive ability of these coatings significantly enhanced through the incorporation of Cu2+ ions. (C) 2016 Elsevier B.V. All rights reserved.
Pretreatment on Electrodepositing of Titanium and Titanium Alloys

屠振密,朱永明,李宁,胡会利,于元春

DOI: https://doi.org/10.3969/j.issn.1007-9289.2010.01.005

2010-01-01

China surface engineering

Abstract:Titanium and titanium alloys are used more and more widely in national economics and defense industry currently.To improve the application characteristics,some surface treatments are adopted.Electrodeposition of metal is a common and convenient method.By electrodeposition of metal,the functionality,decorate properties,anticorrosion and the bonding force with top layer can be enhanced.Pretreatment plays an important role in electrodeposition,and forming proper active film is the key process for pretreatment.The performance of electrodeposition deposit layer depends on some parameters,such as the electrolyte compositions,temperature,pH value,current density,deposit time and so on.
A Study on the Influence of the Electroplating Process on the Corrosion Resistance of Zinc-Based Alloy Coatings

Fan Cao,Jianpeng Wang,Yuli Lian,Yuanhao Wang,Xue Wang,Xiaomin Wang,Aiqing Song,Lei Shi

DOI: https://doi.org/10.3390/coatings13101774

IF: 3.236

2023-10-16

Coatings

Abstract:A comprehensive analysis was conducted to examine the crystal phase composition, surface and cross-section morphology, elemental composition, thickness, and corrosion resistance of coatings. X-ray diffraction (XRD) was employed to investigate the texture and crystal phase of the materials while scanning electron microscopy (SEM) and energy-dispersive spectroscopy (EDS) were utilized to assess the surface and cross-section structure. Additionally, electrochemical techniques were employed to evaluate the corrosion performance. Compared to DC electroplating, the corrosion potential of pulsed galvanized ferroalloy alloy coating increased from −1031 mV to −1008 mV, and the corrosion current density decreased from 3.122 × 10−5 A∙cm−2 to 0.321 × 10−5 A∙cm−2. Moreover, the corrosion rate value of the coating obtained by the pulse rectifier (0.386 × 10−5 g m−2 h−1) was lower than that obtained by the DC power supply (3.75 × 10−5 g m−2 h−1). Additionally, pulsed electrodeposition reduced the iron content of the coating by 0.7%, thereby enhancing its corrosion resistance and flatness. The impedance parameters of the zinc–iron alloy coating acquired through the 30% duty cycle monopulser process exhibit superior performance compared to DC electroplating. Evidently, the monopulse coating’s structure enhances crystal packing density, augments coating thickness, improves adhesion to the substrate interface, and optimizes grain distribution uniformity. These factors are crucial determinants of the corrosion behavior exhibited by Ze–Fe coating.

materials science, multidisciplinary,physics, applied, coatings & films
Influences of the Main Anodic Electroplating Parameters on Cerium Oxide Films

Yang,Yumeng Yang,Xiaoqing Du,Yu Chen,Zhao Zhang,Jianqing Zhang

DOI: https://doi.org/10.1016/j.apsusc.2014.03.078

IF: 6.7

2014-01-01

Applied Surface Science

Abstract:Cerium oxide thin films were fabricated onto 316 L stainless steel via a potentiostatically anodic electrodeposition approach in the solutions containing cerium(III) nitrate (0.05 M), ammonia acetate (0.1 M) and ethanol (10% V/V). The electrochemical behaviors and deposition parameters (applied potential, bath temperature, dissolving 02 and bath pH) have been investigated. Results show that, the electrochemical oxidation of Ce3+ goes through one electrochemical step, which is under charge transfer control. The optimum applied potential for film deposition is 0.8 V. Bath temperature plays a significant effect on the deposition rate, composition (different colors of the film) and surface morphology of the deposits. Due to the hydrolysis of Ce3+, cerous hydroxide is facility to form when the bath temperature is higher than 60 C. The electroplating bath pH is another key role for the anodic deposition of cerium oxide thin films, and the best bath pH is around 6.20. N-2 or O-2 purged into the bath will result in film porosities and O-2 favors cerium oxide particles and film generation. (c) 2014 Elsevier B.V. All rights reserved.
Recent Progress in Electrodeposition of Ni and Ni-based Alloys

CHEN Shuang,LIU Lei,LI Jun,HUANG Shengbiao,TANG Chenglong,ZHONG Cheng

DOI: https://doi.org/10.3969/j.issn.1005-023x.2012.09.023

2012-01-01

Abstract:Electrodeposition technology,structures and properties of Ni and some typical Ni-based(such as Ni-P,Ni-W,Ni-Cr,Ni-Co) alloys are reviewed.The influence of electroplating technology and following treatment processes on the structures,corrosion resistance and abrasive resistance of these alloys′ film are discussed.Electroplating is a complex process,in which almost all the plating elements like the component of plating solution,pH,temperature,and current density can affect the current efficiency,compositions and structures of films,and these effects differ by electroplating system.Heat treatment after electroplating is an effective way to remove film inner stress,eliminate its micro-fissure and enhance its hardness.The existing problems and future trends which based on electroplating mechanism and future application of Ni-based alloys are also discussed.
Current Trends in Organic Electrodeposition Coatings

任碧野,王朝阳,梁栋,童真

DOI: https://doi.org/10.3321/j.issn:0253-4320.2002.09.004

2002-01-01

Abstract:Cationic electrodeposition organic coatings have been rapidly developed since the early 1970s of 20th century featuring their several significant advantages such as low contents of volatile organic compounds(VOCs) and hazardous air pollutants(HAPs),high corrosion resistance,high quality coatings,high material transfer efficiency,especially suitable for complex parts coating.In recent years,research hotspot has turned to organic double layer and multilayer electrocoats as well as polymer polyelectrolytes/oligomeric electrolytes systems.New trends in cationic electrodeposition coatings have received considerable attention due to the significant improvement in physical stability of paints and physicochemical and mechanical properties of coatings.
Electrodeposition of decorative and protective Zn–Fe coating onto low-carbon steel substrate

Z.N. Yang,Z. Zhang,J.Q. Zhang

DOI: https://doi.org/10.1016/j.surfcoat.2005.04.026

IF: 4.865

2006-01-01

Surface and Coatings Technology

Abstract:Cyclic voltammetry and chronoamperometry were performed in conjunction with SEM technique to study the electroplating process of Zn–Fe alloys. The technological parameters for Zn–Fe electroplating have been optimized and the smooth Zn–Fe coatings with high corrosion resistances were obtained. The results also show that, under our experimental conditions, the deposition of Zn–Fe behaved anomalously and followed the mechanism of three-dimensional (3D) nucleation. With the increase of deposition potential, the grain growth changed from progressive to instantaneous. Meanwhile, a new viewpoint was proposed to explain the anomalous co-deposition behavior of Zn–Fe coatings.
Current Status and Development Trend for Cathodic Electrophoretic Coatings

Yanxiong Ke

2003-01-01

Abstract:Cathodic electrophoretic coatings have been widely used for surface treatment of metals for their excellent decorative and protective property and no corrosion metal substrate. Features, classification and development history of cathodic electrophoretic coatings were reviewed, and development trend for cathodic electrophoretic coatings in future was suggested.
SEM Study on Surface Morphology of Cathodic Electrodeposition Epoxy Coatings

梁栋,任碧野,王朝阳,于俊元,童真

DOI: https://doi.org/10.3969/j.issn.0253-4312.2004.01.010

2004-01-01

Abstract:The influence of various painting technical parameters and baking schedules on the surface morphology of CED coatings film is studied by use of Scanning Electronic Microscope (SEM) based on medium and high build epoxy cathodic electrodeposition coatings as a model. It has shown that the film thickness can be controlled by adjustment of voltage and time. Lower voltage, higher baking temperature, and short baking time will be benefited for a smooth and compact coatings film.
Progress in Effects of Electrolysis on Properties of Anodic Coatings on Magnesium Alloys

Zhang Rongfa,Zhang Shufang,Li Wenkui,Xiang Junhuai,Li Mingsheng,Guo Shibo,Duo Shuwang,He Xiangming,Yang Ganlan

DOI: https://doi.org/10.3321/j.issn:1002-185x.2007.z2.203

2007-01-01

Rare Metal Materials and Engineering

Abstract:In the paper, effects of electrolyte on properties of anodic coatings were reviewed in order to lay the foundation for designing and selecting anodizing processes. With development of human awareness on environmental protection, the authors think that the future emphases on studying anodizing electrolyte fie on developing more kinds of electrolytes, which are friendly on environment and human being and considerably improve corrosion resistance of anodic coatings.
The Performance of Zn-Ni Alloy Coating Electrodeposited from Stabilized Bath

Shams Anwar,Faisal Khan,Ya Hui Zhang

DOI: https://doi.org/10.4028/p-qxs29h

2022-04-05

Materials Science Forum

Abstract:A metallic part corrodes when it undergoes electrochemical reactions which cause the surface and structural deterioration of the metal. Through electroplating, metallic components can be protected from corrosion by coating them with Zn-Ni alloys. This study examined the electrodeposition of a Zn-Ni alloy film on a steel substrate from a chloride bath containing ethylene-diamine-tetraacetic acid (EDTA). A Pourbaix diagram using the OLI software was used to determine the stability of the Zn-Ni plating bath and the suppression of hydrogen evolution reaction (HER). Comparing the composition of Zn-Ni coating deposited in the EDTA bath with the pure Zn-Ni coating, the EDTA bath yielded higher deposition thickness and an average crystallite size reduction. The Zn-Ni coating deposited from the EDTA bath has a lower dissolution rate and better corrosion resistance properties than the non-EDTA bath. Polarization tests exhibited that the Zn-Ni alloy deposited from 0.119 mol/l EDTA bath at 20 mA/cm 2 current density showed lower corrosion current (Icorr) and more positive corrosion potential (Ecorr). Atomic force microscopy (AFM) and Vickers microhardness testing were used to characterize the morphological properties, topographic structures, and microhardness of Zn-Ni coatings.
Rapid Electrodeposition and Corrosion Behavior of Zn Coating from a Designed Deep Eutectic Solvent

Jiayi Chen,Mengjun Zhu,Mingtao Gan,Xiuli Wang,Changdong Gu,Jiangping Tu

DOI: https://doi.org/10.3390/met13010172

IF: 2.695

2023-01-01

Metals

Abstract:This work aimed to develop a new type of deep eutectic solvent containing high concentrations of zinc ions as an electrolyte to improve the electrodeposition rate for zinc plating. Two typical deep eutectic solvent systems, choline chloride (ChCl)–urea and ChCl–ethylene glycol (EG), were combined to prepare a stable electrolyte at room temperature with a zinc ion concentration up to 2 M. Cyclic voltammetry experiments of the electrolyte at different temperatures were conducted. The effects of key electrodeposition parameters (bath temperature and current density) on the morphology, structure, and corrosion resistance of zinc coatings deposited on mild steel were investigated. It was found that the crystal orientation of the as-deposited zinc particle is related to the electrodeposition temperature and current density. The experimental results show that the zinc coating deposited at 60 °C and the current density of 4 mA·cm−2 exhibited the most compact and crack-free morphology, thus had the optimum corrosion resistance property.
Influences of Co and process parameters on structure and corrosion properties of nanocrystalline Ni-W-Co ternary alloy film fabricated by electrodeposition at low current density

Weiwei Zhang,Wenzhe Xia,Baosong Li,Mingyuan Li,Ming Hong,Zhen Zhang

DOI: https://doi.org/10.1016/j.surfcoat.2022.128457

IF: 4.865

2022-04-01

Surface and Coatings Technology

Abstract:In this paper, efforts have been dedicated to electrodeposit nanocrystalline Ni-W-Co ternary alloy film on copper substrate through electrodeposition in sulfate-citrate bath. Effects of electrodeposition parameters such as Co ion concentration, applied current density, electrolytic bath pH and deposition time on structural, composition, surface characteristics and corrosion properties of Ni-W-Co alloys were explored. Corrosion and wear behaviors were evaluated. It proved that Ni-W-Co alloy has a uniform, compact and flatter surface, exhibiting colony-like morphology. Amorphous or nanocrystalline structure was formed depending on the process parameters including current density, pH and electrolyte composition. The crystallite size was little affected by Co content but greatly affected by current, bath pH and the duration of plating time. The average roughness Ra was optimized to 4–7 nm. This ternary alloy contains 33 wt% W, 21–60 wt% Ni and 2.8–40 wt% Co. In the alloy, the decrease of nickel content corresponds to the increase of Co and vice versa. W content varied little with the change of electrodeposition conditions. Co content slightly decreases as current density increases. Increasing bath pH greatly decreases the Co contents and increases the Ni content. A ternary complex [M(HWO4)(C6H5O7)]2−(M = Ni, Co) in solution is crucial for the formation of Ni-W-Co alloy. The optimized process parameters for best corrosion and wear resistance were 5–8 mA cm−2, 55 min, 0.1 mol L−1 Co2+ and pH = 6.

physics, applied,materials science, coatings & films
Effects of Electrodeposition Conditions on Composition and Structure of Iron-Cobalt Alloy Foils

XU You,LUO Bei-ping,WU Hu,XIE Qian,REN Bi-ye

2011-01-01

Abstract:The effects of process conditions such as current density,temperature and pH on the composition,cathodic current efficiency,surface morphology and microstructure were studied for Fe-Co alloy foil electroplated on Ti sheet.The bath formulation is as follows:FeSO4·7H2O 40 g/L,CoSO4·7H2O 30 g/L,CoCl2·6H2O 10 g/L,boric acid 30 g/L,trisodium citrate 40 g/L,ascorbic acid 10 g/L,saccharin 1 g/L and sodium dodecyl sulfate 0.1 g/L.The optimal conditions are temperature 50 °C,pH 1.5,and current density 4 A/dm2.The Fe-Co alloy foils are Fe-Co substituted solid solution and face-centered cubic structure with a preferential (111) orientation.The Fe-Co alloy foils have the features of smooth surface,no crack and cavity,compact structure,fine and uniform grain.In addition,the foils are compared of agglomerated small sub-grain.
Effect of Electroplating Bath Composition on Corrosion Resistance of Deposited Cobalt Films

Li Jiang,Pengming Long,Fan Qin,Yundan Yu,Shuting Xu,Zerong Yang,Ziyao Guo,Guoying Wei,

DOI: https://doi.org/10.20964/2020.11.23

IF: 1.541

2020-11-01

International Journal of Electrochemical Science

Abstract:Preparation and corrosion resistance of cobalt films deposited on polycrystalline platinum in different electroplating baths (chloride bath, sulfate bath and chloride-citrate bath) have been studied. Cyclic voltammetry (CV) was used to study the electrodeposition process of cobalt films. Films composition, structure and surface morphology were analyzed by X-ray diffractometer (XRD), atomic force microscope (AFM) and metallographic microscope. Furthermore, the corrosion resistance were measured by potentiodynamic polarization curve and electrochemical impedance spectroscopy (EIS). In different electroplating baths, the shape of cyclic voltammetry curves are similar, where both under-potential deposition behavior and over-potential deposition behavior are presented. The cobalt film obtained from chloride bath is thicker and rougher with acicular shape particles; in sulfate bath, the cobalt grains are spherical shape and the film is smooth with obvious cracks; in chloride-citrate bath, the cobalt grains are seemly much smaller and the film is the smoother and thinner. The component of prepared films in three electroplating baths are mainly cobalt grains with crystal plane of (111), (200) and (220). In 3.5wt.% NaCl solution, the corrosion rate order of deposited cobalt films is v chloride bath < v sulfate bath < v chloride-citrate bath.

electrochemistry
Effect of Voltage and Duty Cycle on Microstructure and Corrosion Resistance of ZrO2 Coating by Cathode Plasma Electrolytic Deposition

D. Zhao,Y. Wang,D. Liu,W. F. Luo,B. C. Wang,Y. B. Yang,Y. Bai,M. Liu,H. D. Wang

DOI: https://doi.org/10.1016/j.ceramint.2023.11.278

IF: 5.532

2023-01-01

Ceramics International

Abstract:Power parameters are of importance to determine the microstructure and property of coatings deposited by cathode plasma electrolytic deposition (CPED). In the present study, the effect of power parameters including voltage and duty cycle on the microstructure and anti -corrosion property of zirconia (ZrO2) CPED-coatings was investigated. The results suggested that the as -deposited coatings consisted of t-ZrO2 and m-ZrO2, while the content of t-ZrO2 exceeded 50 %. The content of t-ZrO2 increased with the increase of voltage and decreased with the increase of duty cycle, reaching a maximum of 89.9 %. In addition, as the voltage and duty cycle increased, the porosity of the coating increased from 3.7 % to 15.5 %. Due to the high t-ZrO2 content, high thickness and relatively dense structure, the coatings deposited at 250 V had a superior corrosion resistance in 3.5 wt% NaCl solution. This work will provide a guideline for tailoring high performance ZrO2 CPED-coatings.
The effects of main salt concentrations and deposition voltages on the structures and properties of cathode plasma electrolytic deposited Cr2O3 coatings

Shuguang Zhang,Wenjing Xiong,Jin Zhang,Yong Lian,Yedong He

DOI: https://doi.org/10.1088/2053-1591/ab4bde

IF: 2.025

2019-01-01

Materials Research Express

Abstract:In this paper, Cr2O3 coatings were prepared on the 7075 Al alloys by cathode plasma electrolytic deposition (CPED) method in the trivalent chromium (CrCl3 center dot 6H(2)O) electrolytes. The effects of the concentrations of the CrCl3 center dot 6H(2)O and the deposition voltages on the phases and structures of the coatings were investigated by SEM, EDS, XRD and electrochemical test. The results showed that the electrolyte of 30 g l(-1) CrCl3 center dot 6H(2)O was benefit for the formation of a coating with non-rough and sintered structure. The coating formed at the voltage of 240 V was relatively dense and showed better resistance to the corrosion. The formation mechanism of the Cr2O3 coating was disclosed.

Factors Influencing Cathodic Electrodeposition Coating Process

Effect of Process Parameters on Electrodeposition Process of Co-Mo Alloy Coatings

The Study of Thin Film High–voltage Li-Ion Cathodes to Reveal Surface Reactions and Coating Performance

Influence of Electrodeposition Conditions on the Microstructure and Corrosion Resistance of Zn–Ni Alloy Coatings from a Deep Eutectic Solvent

Electrochemical Performance of Electroactive Poly(Amic Acid)-Cu2+ Composites

Pretreatment on Electrodepositing of Titanium and Titanium Alloys

A Study on the Influence of the Electroplating Process on the Corrosion Resistance of Zinc-Based Alloy Coatings

Influences of the Main Anodic Electroplating Parameters on Cerium Oxide Films

Recent Progress in Electrodeposition of Ni and Ni-based Alloys

Current Trends in Organic Electrodeposition Coatings

Electrodeposition of decorative and protective Zn–Fe coating onto low-carbon steel substrate

Current Status and Development Trend for Cathodic Electrophoretic Coatings

SEM Study on Surface Morphology of Cathodic Electrodeposition Epoxy Coatings

Progress in Effects of Electrolysis on Properties of Anodic Coatings on Magnesium Alloys

The Performance of Zn-Ni Alloy Coating Electrodeposited from Stabilized Bath

Rapid Electrodeposition and Corrosion Behavior of Zn Coating from a Designed Deep Eutectic Solvent

Influences of Co and process parameters on structure and corrosion properties of nanocrystalline Ni-W-Co ternary alloy film fabricated by electrodeposition at low current density

Effects of Electrodeposition Conditions on Composition and Structure of Iron-Cobalt Alloy Foils

Effect of Electroplating Bath Composition on Corrosion Resistance of Deposited Cobalt Films

Effect of Voltage and Duty Cycle on Microstructure and Corrosion Resistance of ZrO2 Coating by Cathode Plasma Electrolytic Deposition

The effects of main salt concentrations and deposition voltages on the structures and properties of cathode plasma electrolytic deposited Cr2O3 coatings