Abstract:The 2195 Al-Cu-Li alloy is widely utilized for the fabrication of key aerospace vehicle components; hence, an in-depth understanding of its hot deformation behavior is essential for consistently achieving high-performance products. In this study, isothermal compression tests were performed on 2195 Al-Cu-Li alloy ingots in the temperature and strain rate ranges of 250–500 °C and 10 −3 -1 s −1 , respectively. A processing map was established to predict the workability under different conditions. The corresponding microstructures were examined to reveal their hot deformation mechanism. Results demonstrated that the processing map was divided into four distinct domains. The unstable zone was located in the 250–375 °C/10 −1.5 -1 s −1 and 250–275 °C/10 −2.5 –10 −1.5 s −1 , temperature/strain rate regimes, in which deformation bands and flow localization were observed. The deformation bands blocked dislocations and compromised the dynamic recrystallization (DRX) behavior, hence damaging the microstructure. Further, large coarse T 1 phases precipitated in the 325–410 °C/10 −2.5 –10 −3 s −1 regime, which led to the formation of heterogeneities in the microstructure, corresponding to a minimum workability in the processing map. The optimal hot-working domain for the 2195 alloy was determined to be 460–500 °C/10 −3 –10 −2 s −1 , and the dominating hot deformation mechanisms were DRX and dynamic recovery (DRV). Specifically, continuous and discontinuous DRX behaviors dominated in the 300–400 °C/10 −3 s −1 and 450–500 °C/10 −3 s −1 regimes, respectively. DRX gradually weakened as the strain rate increased at 500 °C. Further, the weakening of DRX was only minimally affected by temperature at 400–500 °C during high-speed deformation (1 s −1 ). The results reported herein can provide valuable insights into the hot working of Al-Cu–Li alloys.

Hot deformation behavior and processing map of 6069 aluminum alloy

Study of Hot Deformation Behavior of 6082 Aluminum Alloy

Constitutive behavior and novel characterization of hot deformation of Al-Zn-Mg-Cu aluminum alloy for lightweight traffic

Hot Deformation and Processing Map of As-Homogenized Mg–9Gd–3Y–2Zn–0.5Zr Alloy

Hot deformation characteristics and processing maps of AA7075-H18 alloy sheet under hot forming process conditions

Hot Working Property Study of 7055 Aluminum Alloy Based on Hot Shear-Compression Deformation

Hot Deformation Behavior and Processing Map of Al-Zn-Mg-Cu-Zr Alloy

Hot tensile deformation behavior and microstructure evolution of 7075 aluminum alloy sheet

Investigation on hot deformation behavior of 2050 Al-Cu-Li alloy

Characterization of Hot Deformation Behavior and Processing Maps of Homogenized Al-Mg-Si-Sc-Zr Alloys

Modified constitutive model and workability of 7055 aluminium alloy in hot plastic compression

Hot Deformation Behavior of 2026 Aluminum Alloy During Compression at Elevated Temperature

Hot Deformation Behavior and Microstructure Evolution of 6063 Aluminum Alloy Modified by Rare Earth Y and Al-Ti-B Master Alloy

Hot Deformation Characteristics and Processing Parameter Optimization of Al–6.32Zn–2.10Mg Alloy Using Constitutive Equation and Processing Map

Hot deformation behavior and microstructural evolution of the Al-Cu-Li alloy: A study with processing map

The Study on Forming Property at High Temperature and Processing Map of 2219 Aluminum Alloy

Study on Hot Compression Deformation and Processing Map of Mg-6Al-2Si-1.5Er Mg Alloy

Hot Workability and Microstructure Evolution of Homogenized 2050 Al-Cu-Li Alloy during Hot Deformation

Constitutive modeling of deformation in high temperature of a forging 6005A aluminum alloy

Hot Deformation Behavior of Homogenized Al-7.8Zn-1.65Mg-2.0Cu (wt.%) Alloy

Hot deformation characteristics and processing parameter optimization of 2219 Al alloy using constitutive equation and processing map