Tribological Properties of Stainless Steel Modified with Dual- and Co-implantation of Co+C Ions

Jun-xia GUO,Qiu-long CHEN,Xun CAI,Cheng-shu CHEN

DOI: https://doi.org/10.3321/j.issn:1004-0595.2006.02.008

2006-01-01

Abstract:Cobalt and carbon ions were dual- and co-implanted into austenitic stainless steel by a metal vapor vacuum arc (MEVVA) ion source with total dose of 6 × 1017 ions/cm and 8 × 10 ions/cm. Microstructural properties of the implanted surface were investigated by Auger electronic spectroscopy and microhardness test, and tribological performance of the modified layer were carried out on a pin-on-disc tribometer and their friction and wear properties were discussed. Analysis of AES results show that a Co + C co-existed zone were obtained by dual- and Co-implantation of Co + C, leading to broadened concentration profiles and extended strengthened depth. Both dual- and co-implantation of Co + C greatly increased the near-surface hardness and improved the wear resistance of stainless steel. Compared with the unimplanted sample, wear volume loss was reduced by 82% with dual-implantation and by 76%-97% with co-implantation. Moreover, co-implantation of Co + C with higher dose was more effective than dual-implantation for improving wear resistance.