Phase Constitution and Microstructure of Ni-Al Intermetallic Compounds Fabricated by Thermal Explosion

崔洪芝,魏娜,赫庆坤,白斌

DOI: https://doi.org/10.13289/j.issn.1009-6264.2013.07.006

2013-01-01

Abstract:Thermal explosion method was employed to produce Ni-Al intermetallic compounds using elemental Ni and Al powder mixture.The phase constitution,microstructure and microhardness of the products were investigated by means of X-ray diffraction,electron probe microanalysis and microhardness test.The results indicate that a uniform dendritic structure consisting of single NiAl is obtained with the composition of Ni∶Al=1∶1(molar ratio).When the molar ratio of Ni∶Al is 3∶1,the phases are mainly composited of β-NiAl phase with dendritic structure,γ′-Ni3Al phase with irregular block and net-like morphology,γ′-Ni3Al phase with irregular and pointed strip-like morphology and M-NiAl phase with needle-like and lath-shaped morphology.The precipitation of γ′-Ni3Al causes the stress field,the NiAl is a Ni-rich phase and the cooling process is non-equilibrium,these are all beneficial for the β-NiAl phase transforming to M-NiAl phase.